Linear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Description
The linear electrcial properties of 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
In order to prepare glasses two compounds: Bi2VO5.5 and SrB4O7 were synthesized via a solid state reaction route. The Bi2VO5.5 was synthesized from the stoichiometric mixture of initial powders of Bi2O3 and V2O5 which were ball-milled in pure acetone for 6 h at room temperature. The milling was performed in steps of 1 h with rest intervals of 10min. The mixture was heated up to 1020K in air and kept at this temperature for 24 h. The heating and cooling rate was of 50K h-1. The obtained powder was checked by X-ray diffraction method. The SrB4O7 was synthesized from the stoichiometric mixture of analytical grade SrCO3 and H3BO3 which were mashed in a mortar. Next the mixture was heated up to 1073K and kept at this temperature for 12 h. Samples of a composition of 50Bi2VO5.5–50SrB4O7 (in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at 1373K for 2 h. The melts were poured onto a preheated (573 K) brass plate and pressed by another plate to obtain flat circular disks of 1–2mm thickness and 20–30mm diameter.
For the electrical measurements gold electrodes were evaporated at the preheated samples. Impedance measurements were carried out in the temperature range from 153 K to 423 K, in the frequency range from 10mHz to 1 MHz and with the ac voltage of 1 Vrms with Concept 40 broadband dielectric spectrometer.
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2015
- Verification date:
- 2021-06-21
- Dataset language:
- English
- Fields of science:
-
- materials engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/fdkb-4c39 open in new tab
- Verified by:
- Gdańsk University of Technology
Keywords
References
- publication STRUKTURA ORAZ WŁAŚCIWOŚCI ELEKTRYCZNE MATERIAŁÓW SZKLISTYCH ZAWIERAJĄCYCH GRANULE FERROELEKTRYKA Bi2VO5,5
- publication Mixed ionic-electronic conductivity and structural properties of strontium-borate glass containing nanocrystallites of Bi2 VO5.5
Cite as
Authors
seen 88 times