Goal of the present research was to investigate the influence of V2O5 additive on the structure and dielectric properties of BiNbO4 ceramics. To fabricate BiNbO4 ceramics with V2O5 added the solid state reaction route and pressureless sintering was utilized. Thus obtained ceramics was characterized in terms of its microstructure (SEM), chemical composition (EDS), phase composition and crystalline structure (X-ray phase and structural analysis, respectively). Also dielectric properties in both temperature and frequency domains were investigated. The impedance spectroscopy was utilized for dielectric characterization and the measurements of complex impedance were performed within the frequency range =10Hz–1MHz and temperature range T =RT-550C. It was found that V2O5 additive changed slightly lattice parameters of BiNbO4 ceramics, decreased porosity of samples and revealled relaxation phenomena within the frequency ranges =102–103 Hz and =105–106 Hz at temperature T>285C.
Citations
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Authors (4)
-
Katarzyna Osińska dr
-
Małgorzata Adamczyk dr hab.
Cite as
Full text
- Publication version
- Accepted or Published Version
- DOI:
- Digital Object Identifier (open in new tab) 10.2478/amm-2013-0180
- License
-
open in new tab
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
ARCHIVES OF METALLURGY AND MATERIALS
no. 58,
pages 1387 - 1390,
ISSN: 1733-3490 - Language:
- English
- Publication year:
- 2013
- Bibliographic description:
- Lisińska-Czekaj A., Czekaj D., Osińska K., Adamczyk M.: Effects of V2O5 Additive on Structure and Dielectric Properties of BiNbO4 Ceramics// ARCHIVES OF METALLURGY AND MATERIALS -Vol. 58,iss. 4 (2013), s.1387-1390
- DOI:
- Digital Object Identifier (open in new tab) 10.2478/amm-2013-0180
- Verified by:
- Gdańsk University of Technology
seen 130 times
Recommended for you
STUDY OF CuO AND V2O5 EFFECT ON IR SPECTRA OF POLYCRYSTALLINE BISMUTH NIOBATE
- I. Kuźniarska-Biernacka,
- A. Lisińska-Czekaj,
- D. Czekaj