Hydrogen Damage in Superaustenitic 904L Stainless Steels

J. Michalska; B. Chmiela; Jerzy Łabanowski; W. Simka

doi:10.1007/s11665-014-1044-2

Hydrogen Damage in Superaustenitic 904L Stainless Steels

Abstract

results on the influence of hydrogen on corrosion resistance and of hydrogen embrittlement of 904L superaustenitic stainless steel were investigated. The cracking behavior was studied by performing a slow strain rate test in synthetic seawater under varying cathodic polarization conditions. The results showed that the steel’s plasticity varied with the applied cathodic current density. Significant reductions in ductility were found, indicating its susceptibility to hydrogen-assisted fracture at current density of 20 mA/cm2. Fractographical examinations showed that an increase in hydrogenation current density causes a stepwise decrease in ductility on the fracture surface. The effect of hydrogen on passivity and on pitting corrosion resistance was qualified with the polarization curves registered in synthetic seawater. The conclusion is that hydrogen may affect the passive film stability and thus may decrease the corrosion resistance of the studied steel. The presence of hydrogen increases corrosion current density and decreases the potential of the film breakdown. It was also found that the degree of the susceptibility to hydrogen degradation was dependent on the hydrogen charging conditions.

Citations

1 2

CrossRef
0

Web of Science
1 7

Scopus

Authors (4)

J. Michalska
- Institute of Materials Science .
B. Chmiela
- Institute of Materials Science .
Jerzy Łabanowski prof. dr hab. inż.
W. Simka
- Institute of Materials Science .

Cite as

Full text

download paper

downloaded 26 times

Publication version: Accepted or Published Version
DOI:: Digital Object Identifier (open in new tab) 10.1007/s11665-014-1044-2
License: open in new tab

full content of the article see on external site open in new tab

Keywords

FRACTOGRAPHY HYDROGEN DAMAGE PITTING SLOW STRAIN RATE TEST (SSRT) SUPERAUSTENITIC STAINLESS STEE

Details

Category:: Articles
Type:: artykuł w czasopiśmie wyróżnionym w JCR
Published in:: JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE no. 23, edition 8, pages 2760 - 2765,
ISSN: 1059-9495
Language:: English
Publication year:: 2014
Bibliographic description:: Michalska J., Chmiela B., Łabanowski J., Simka W.: Hydrogen Damage in Superaustenitic 904L Stainless Steels// JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE. -Vol. 23, iss. 8 (2014), s.2760-2765
DOI:: Digital Object Identifier (open in new tab) 10.1007/s11665-014-1044-2
Verified by:: Gdańsk University of Technology