Influence of High Temperature Oxidation on Hydrogen Absorption and Degradation of Zircaloy-2 and Zr 700 Alloys
Abstract
The present research was aimed at determining the effects of the oxide layers on hydrogen absorption, microstructure and mechanical properties of the Zircaloy- 2 and Zr 702 alloys. The oxidation was made at 350 °C, 700 °C and 900 °C for 10 to 30 min in laboratory air, followed by hydrogen cathodic charging for 72 h and annealing at 400 °C for 4 h. The slow strain rate tests were carried out on oxidized, charged and annealed specimens. The oxidation resulted in thick and cracked, more for Zr 702 alloy, layer. After oxidation at 350 °C, the appearance of hydrides in Zircaloy-2 and absence of hydrides in Zr 702 alloy were observed. After oxidation at high temperatures no current flow was noticed at applied voltage up to 5 V, and no hydrogen or hydrogen cracks. The observed effects were attributed to the phase structure of investigated alloys at low hydrogen content.
Citations
-
3
CrossRef
-
0
Web of Science
-
2
Scopus
Authors (5)
Cite as
Full text
- Publication version
- Accepted or Published Version
- License
-
open in new tab
Keywords
Details
- Category:
- Articles
- Type:
- artykuł w czasopiśmie wyróżnionym w JCR
- Published in:
-
HIGH TEMPERATURE MATERIALS AND PROCESSES
no. 38,
pages 8 - 15,
ISSN: 0334-6455 - Language:
- English
- Publication year:
- 2019
- Bibliographic description:
- Zieliński A., Cymann A., Gumiński A., Hernik A., Gajowiec G.: Influence of High Temperature Oxidation on Hydrogen Absorption and Degradation of Zircaloy-2 and Zr 700 Alloys// HIGH TEMPERATURE MATERIALS AND PROCESSES. -Vol. 38, (2019), s.8-15
- DOI:
- Digital Object Identifier (open in new tab) 10.1515/htmp-2017-0074
- Verified by:
- Gdańsk University of Technology
seen 224 times
Recommended for you
Hydrogen degradation of pre-oxidized zirconium alloys
- A. Szoka,
- G. Gajowiec,
- A. Zieliński
- + 3 authors
Oxidation and hydrogen behavior in Zr-2Mn alloy
- N. Zienkiewicz,
- J. Paradowska,
- W. Serbiński
- + 3 authors