Abstract
Fatigue behaviour of SLM 18Ni300 steel under proportional bending-torsion loading is studied. The fatigue tests are conducted under pulsating loading conditions using tubular specimens with a transversal circular hole. Three ratios of the normal stress to shear stress are considered, namely σ/τ=4,σ/τ=2 and σ/τ = 4/3. Crack initiation sites were found for two diametrically opposite points around the hole, whose locations are governed by the loading scenario. Crack angles at the early stage of growth were successfully predicted from the first principal direction at the nodes with maximum values of the first principal stress at the hole. Fatigue crack initiation life was estimated based on the SWT parameter, defined from uniaxial low-cycle fatigue tests performed for smooth standard specimens under fully reversed strain-controlled conditions. Overall, predicted lives are in agreement with the experiments.
Citations
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Authors (6)
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Monographic publication
- Type:
- rozdział, artykuł w książce - dziele zbiorowym /podręczniku w języku o zasięgu międzynarodowym
- Published in:
-
Structural Integrity
no. 25,
pages 161 - 168,
ISSN: 2522-560X - Title of issue:
- Structural Integrity and Fatigue Failure Analysis strony 161 - 168
- Language:
- English
- Publication year:
- 2022
- Bibliographic description:
- Branco R., Costa J. D., Ferreira J. A. M., Capela C., Berto F., Macek W.: Multiaxial Fatigue Behaviour of SLM 18Ni300 Steel// Structural Integrity and Fatigue Failure Analysis/ : , 2022, s.161-168
- DOI:
- Digital Object Identifier (open in new tab) 10.1007/978-3-030-91847-7_16
- Verified by:
- Gdańsk University of Technology
seen 99 times
Recommended for you
Effect of bending-torsion on fracture and fatigue life for 18Ni300 steel specimens produced by SLM
- W. Macek,
- R. Masoudi Nejad,
- S. Zhu
- + 5 authors
Notch fatigue analysis and life assessment using an energy field intensity approach in 7050-T6 aluminium alloy under bending-torsion loading
- R. Branco,
- J. D. Costa,
- L. Borrego
- + 2 authors
On the use of uniaxial one-parameter damage laws for estimating fatigue life under multiaxial loading
- R. Branco,
- J. D. Costa,
- L. Borrego
- + 3 authors
Load path sensitivity and multiaxial fatigue life prediction of metals under non-proportional loadings
- Q. Deng,
- S. Zhu,
- X. Niu
- + 3 authors