The impact of the crystallinity on structural, thermal, and in vitro dissolution properties were examined for Na2O- CaO-Nb2O5/MgO-P2O5 glasses/glass-ceramics. Glass-ceramics were synthesized via a spontaneous crystallization process. The Nb content in the materials increased with melting temperature, furthermore, the crystallinity is proportional to the Nb content. The presence of crystalline niobates and phosphates is confirmed...

In vitro dissolution, structure, and thermal properties of the glass series Na2O-MgOsingle bondCaOsingle bondNb2O5 -Al2O3-P2O5 were studied. The dissolution behavior in phosphate-buffered saline (PBS) confirmed the potential bioactive properties of tested glasses. The dissolution process was found to depend on the Al, Nb, and Mg contents. Al, respectively, suppresses the Nb and accelerates the Mg release process from the glasses....

A set of fifteen calcium-phosphate-silicate glass samples, varying in alkali, magnesium, silicon, and nitrogen content, was prepared, and their structural, thermal, and in vitro dissolution properties were analyzed. Infrared spectroscopy showed a high degree of depolymerization of the silicate network consisting mainly of Q2 and Q3 units. Thermal analysis showed that the silicon content primarily affects both the glass transition...