Open Research Data
-
Raman studies of 3D printed CB-PLA samples after microwave treatment
Open Research DataThis dataset contains Raman spectroscopy analyses of microwave-activated carbon-black doped polylactic acid 3D printed electrodes.
-
SEM micrographs of 3D printed CB-PLA samples topography after microwave treatment
Open Research DataThis dataset contains the electrochemical studies on microwave-activated carbon-black doped polylactic acid 3D printed electrodes.
-
SEM micrographs of 3D printed CB-PLA samples topography after microwave treatment
Open Research DataThis dataset contains the SEM micrographs of carbon-black doped polylactic acid 3D printed electrodes, after microwave treatment to activate the electrode surfaces. FEI Quanta 250 FEG SEM was used for these analyses. Samples were treated with CEM reactor or microwave oven.
-
Valorisation of bioplastics synthesised by liquefaction of celluloseusing hetero- and homogeneous catalysts
Open Research DataThe purpose of the present study was to test the effectiveness of a heterogeneous catalyst such as Nafion ion-exchange resin on the cellulose liquefaction process. The results obtained were compared with the bio-polyols obtained in a conventional way, using a homogeneous catalyst (sulfuric acid (VI)). Depending on the catalyst used and the temperature...
-
Valorization of bio-based polyols synthesized via biomass liquefaction
Open Research DataAs the properties of polyols have a huge impact on the properties of manufactured polyurethanes, this study aims to determine the influence of polyethylene glycols with different molecular masses on the course of the biomass liquefaction process and bio-polyol properties. The obtained polyols were characterized by rheological studies. To confirm the...
-
Influence of bio-polyols with different molecular weight on properites of PUR-PIR foams
Open Research DataThis work attempts to validate the possibility of replacing petrochemical polyols with previously synthesized bio-polyols and their impact on the structure and properties of rigid polyurethane-polyisocyanurate (PUR-PIR). The influence of bio-polyols addition on foam properties was investigated by mechanical testing, Fourier transform infrared spectroscopy...
-
Validation of polyurethane-wood composites properties
Open Research DataThis study focuses on the development of the PU-WC manufacturing method, the determination of properties of this type of composite, and the indication of its potential application. The mechanical properties of PU-WC were characterized by flexural tests. To determine the thermal properties, dynamic mechanical analysis (DMA) and thermogravimetric analysis...
-
Broadband dielectric spectroscopy studies of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains broadband dielectric spectroscopy studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different...
-
Thermal analyses of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains thermal analyses (TGA, DTG, DSC) studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different...
-
Topography studies of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains topography studies with scanning electron microscope of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material...
-
Rheology studies of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains MFR/MVR (melt flow rate) rheology studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The study aims to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
Electrochemical analyses of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains cyclic voltammetry studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
Physicochemical studies (Raman) of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains Raman spectroscopy studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
Physicochemical studies (Raman, XRD) of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains physico-chemical examination of a new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques include Raman spectroscopy and X-ray diffraction...
-
Mechanical studies of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains mechanical tests carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques was dynamic mechanical analysis (DMA). The measurements...
-
Rheology studies of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains rheology measurements carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques was performed by melt mass-flow rates (MFR)....
-
Thermal stability analysis of poly(lactic acid)-carbon black-nanodiamond composite
Open Research DataThis dataset contains thermal stability tests carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques include: thermogravimetric analysis (TGA)...
-
bio-based polyester polyols - chemical structure of Miniatura 4 proper samples
Open Research DataPresented results are related with project MINIATURA 4 realization. At the document, the chemical structure of bio-based polyester polyols (poly(propylene-co-propan-1,2,3-triol succinate)s) are presented as analysis of FTIR and H NMR spectroscopy.
-
Bio-based polyester polyols for polyurethane foams - chemical structure of reference sample
Open Research DataPresented dataset includes the results of FTIR and H NMR spectroscopy of bio-based polyester polyol - poly(propylene succinate) (reference sample for materials obtained during MINIATURA 4 project realization).
-
Bio based PUR-PIR foams thermal degradation (TG) and isoconversional kinetics
Open Research DataIn the present work, we perform a thorough thermogravimetric (TG) analysis of the bio-based polyurethane – polyisocyanurate (PUR-PIR) foams in both nitrogen and oxygen atmosphere. A sustainable element of the foam was a biopolyol obtained via acid-catalyzed liquefaction of Zostera Marina and Enteromorpha Algae biomass. Based on isoconversional analysis...
-
The effect of different accelerators on the reclaiming efficiency of ground tire rubber
Open Research DataThe presented results concern the influence of different accelerators on the reclaiming efficiency of ground tire rubber (GTR). All the specimens were prepared using a two-roll mill and each sample was prepared in the same manner. Samples were submitted to curing analysis via Rheometer Monsanto 100S after 24 hours of aging. The attached data are related...
-
Curing characteristics of ground tire rubber modified by commercial additives
Open Research DataThe presented results show the influence of commercially available bitumen and transoctenamer rubber (TOR) on the curing behavior of GTR treated by a peroxide. Samples were prepared using a two-roll mill– all in the same manner. After 24 hours of aging at ambient conditions, they were submitted to the curing analysis via Rheometer Monsanto 100S. The...
-
Curing characteristics and Mooney viscosity of reclaimed rubbers
Open Research DataPresented data shows the difference in curing characteristics and Mooney’s viscosity between commercially available reclaimed rubbers and ground tire rubber (GTR) with specific particle size distribution cured with the same curing system and with the same manner. Samples were prepared using a two-roll mill. After 24 hours of aging at ambient conditions,...
-
The impact of carbon black particle size on curing characteristics of GTR modified with bitumen
Open Research DataPresented data shows an impact of particle size of GTR and three different loadings of carbon black on curing characteristics of GTR modified with bitumen. Samples were prepared using a two-roll mill – all in the same manner. After 24 hours of stabilization at ambient conditions they were submitted to the curing analysis via Rheometer Monsanto 100S....