Results after grinding C45 steel

The database contains results from nanoindenter, scanning microscope and also X-ray diffractometer. To determine the residual stresses and the size of the crystallites in the ferrite grains in the grinded surface layer, the Williamson Hall analysis of the X-ray diffraction patterns was performed. XRD diffraction patterns were also used to perform a...

Microstructure of cross-sections of samples after laser treatment for the article entitled "Mechanical and corrosive properties of Ti13Nb13Zr alloy subjected to laser treatment with MWCNTs coatings"

SEM examination of surface layer of C45 steel after grinding on defferent depth

Ferrite examination for the medium carbon structural steel with low content of Mn, Si, Cu, Cr and Ni after its grinding to a depth of 2 µm, 8 µm, 14 µm and 20 µm, at constant wheel circumferential speed of vs = 25 m/s and constant feed rate vft = 1 m/min. It was shown that the grinding of C45 steel causes strong work hardening of ferrite in surface...