Low velocity impact behaviour of nano-SiO2 enhanced carbon fibre/epoxy composites for naval applications is reported. Epoxy resin matrix was enhanced by 1- 8 wt% SiO2 nanoparticles, based on industrial surface-modified nanosilica. Impact parameters: force, deformation, energy, damage size were recorded. The most pronounced effect was damage size decrease; e.g. ∼28% recorded by infrared thermography and X-ray computed radiography...
Mechanical and Microstructural Characterization of TIG Welded Dissimilar Joints between 304L Austenitic Stainless Steel and Incoloy 800HT Nickel Alloy
In this article, the mechanical properties and microstructure of 304L austenitic stainless steel/Incoloy 800HT nickel alloy dissimilar welded joints are investigated. The joints were made of 21.3 mm × 7.47 mm tubes using the TIG process with the use of S Ni 6082 nickel filler metal. No welding imperfections were found and high strength properties of joints were obtained, meeting the assumed acceptance criteria of the product’s...
This study presents results of experimental tests on quality of dissimilar welded joints between 316L austenitic and 2304 lean duplex stainless steels, welded without ceramic backing. Fiber laser welded butt joints at a thickness of 8 mm were subjected to non‐destructive testing (visual and penetrant), destructive testing (static tensile test, bending test, and microhardness measurements) and structure observations (macro‐ and...