La-Sr-Ce-Ni-Ti (LSCNT) based ceramics sample was manufactured by standard solid state reaction.Prepared powder was pressed into pilled and sintered in a furnace in air atmosphere for 10h. Annealing temperature was 1200 Celsius degree. To calculate chemical composition and determine valence states of the elements, X-Ray photoemission spectroscopy (XPS) analysis were performed. Measurements were conducted at room temperature under a pressure below 1.1 × 10−9 mBar. The photoelectrons were excited by an Mg-Kα X-Ray anode operated at 15 keV and 300 W. Omicron Argus hemispherical electron analyser with a round aperture of 4 mm was used for the analysis of energy of the emitted photoelectrons. Th high resolution scans were performed for each element (La3d, Ni2p, Ti2p, Sr3d and Ce3d).
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - Raw data:
- Data contained in dataset was not processed.
- Software:
- origin
Details
- Year of publication:
- 2021
- Verification date:
- 2021-07-15
- Creation date:
- 2019
- Dataset language:
- English
- Fields of science:
-
- materials engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/7crn-wp11 open in new tab
- Verified by:
- Gdańsk University of Technology
Keywords
Cite as
Authors
seen 102 times