Search
Description
Electrical properties of silicate-lead glasses doped with different content of iron oxide was studied. The set of glass samples were prepared with the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573 K and formed into button-shaped samples. Afterwards pellets were annealed at 673K, cooledwith the furnace and polished to the thickness of about 1mm. For the electrical conductivity measurements, golden electrodes were evaporated at both sides of preheated samples in vacuum. The linear impedance spectra were measured in the frequency range of 1 MHz to 1 MHz and in the temperature range of 153 K to 423 K by Novocontrol Concept 40 broadband dielectric spectrometer. Detailed information you can find in: http://dx.doi.org/10.1016/j.ssi.2013.10.008
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2014
- Verification date:
- 2021-05-05
- Dataset language:
- English
- Fields of science:
-
- materials engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/q023-zz87 open in new tab
- Verified by:
- Gdańsk University of Technology
Keywords
References
Cite as
Authors
seen 116 times