Ceramic samples based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by solid state reaction. After sintring in a furnance, samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology. XPS analysis were performed at room temperature under a pressure below 1.1 × 10−9 mBar. The photoelectrons were excited by an Mg-Kα X-Ray anode operated at 15 keV and 300 W. Omicron Argus hemispherical electron analyser with a round aperture of 4 mm was used for the analysis of emitted photoelectrons. Measurements were carried out in a constant analyser energy (CAE) mode with pass energy equal 50 eV. To remove contaminations and oxides, the surface was etched before the measurement. Argon ion gun with energy up to 5 keV was used for 5 min. etching. In this dataset Ba3d, Ba4d and Ba4p high resolution spectra for samples are presented.
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2021
- Verification date:
- 2021-07-19
- Creation date:
- 2019
- Dataset language:
- English
- Fields of science:
-
- materials engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/d9ba-0928 open in new tab
- Verified by:
- Gdańsk University of Technology
Keywords
Cite as
Authors
seen 119 times