Linear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K measured with impedance spectroscopy method at low temperature region
Description
The linear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
Bi2VO5.5 glas-ceramic was prepared from appropriate amounts of Bi2O3 and V2O5 powders. The melting was conducted in alumina crucibles at 1173 K for few minutes. The melt was poured onto a preheated (573 K) brass plate and pressed by another plate to obtain flat circular disks. Next samples were annealed at 423 K.
For the electrical measurements gold electrodes were evaporated at the preheated samples. Impedance measurements were carried out in the temperature range from 153 K to 423 K, in the frequency range from 10mHz to 10 MHz and with the ac voltage of 1 Vrms with Concept 40 broadband dielectric spectrometer.
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2015
- Verification date:
- 2021-07-14
- Dataset language:
- English
- Fields of science:
-
- materials engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/s1w7-p339 open in new tab
- Verified by:
- Gdańsk University of Technology
Keywords
References
- publication STRUKTURA ORAZ WŁAŚCIWOŚCI ELEKTRYCZNE MATERIAŁÓW SZKLISTYCH ZAWIERAJĄCYCH GRANULE FERROELEKTRYKA Bi2VO5,5
- publication Nonlinear and linear impedance of bismuth vanadate ceramics and its relation to structural properties
Cite as
Authors
seen 101 times