SEM examination of surface layer of C45 steel after grinding on defferent depth

Description

Ferrite examination for the medium carbon structural steel with low content of Mn, Si, Cu, Cr and Ni after its grinding to a depth of 2 µm, 8 µm, 14 µm and 20 µm, at constant wheel circumferential speed of vs = 25 m/s and constant feed rate vft = 1 m/min. It was shown that the grinding of C45 steel causes strong work hardening of ferrite in surface layer without phase transformation.

Dataset file

SEM.zip

114.5 MB, S3 ETag d944501003ea2e6f73ac33227daee8f1-1, downloads: 70

The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

download

File details

License:: open in new tab

CC BY-NC-SA

Non-commercial - Share-alike
Raw data:: Data contained in dataset was not processed.

Details

Year of publication:

2021

Verification date:

2021-05-14

Dataset language:

English

Fields of science:

materials engineering (Engineering and Technology)
mechanical engineering (Engineering and Technology)

DOI:

10.34808/d3az-hz26

Verified by:

Gdańsk University of Technology

Keywords

References

Cite as

Authors

seen 175 times

Search