The dataset includes SEM images of Ni-Mo2CTx/Mo2Ga2C catalysts before and after the dry reforming of methane.
MAX matrice Mo3AlC2 was purchased from Luoyang Tongrun Info Technology, China.
MXene material was prepared via selective etching of aluminium using hydrofluoric acid (50%) for 96 h at room temperature. After the etching, the powders were flirted and washed with water and ethanol until pH reached 6. Then, the MXene was dried under vacuum at 50˚C for 24 h.
Nickel catalyst was prepared via impregnation of previously prepared Mo2CTx/Mo2AlC2 with aqueous nickel nitrate solution and drying at 50 deg. C under vacuum.
Catalytic process parameters:
- composition of intel stream: methane:carbon dioxide = 1:1
- temperature - 800 deg. C
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2022
- Verification date:
- 2022-09-20
- Creation date:
- 2021
- Dataset language:
- English
- Fields of science:
-
- chemical sciences (Natural sciences)
- chemical engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/f7ev-an77 open in new tab
- Funding:
- Verified by:
- Gdańsk University of Technology
Keywords
References
- dataset XRD data of V2AlC, Mo3AlC2, Mo3CTx and V2AlCTx
- dataset SEM images of Ni-Mo2CTx/Mo2Ga2C before and after catalytic dry reforming of methane
- dataset Temperture-programmed reduction (H2-TPR) of Ni-Mo2CTx_Mo2Ga2C and Ni-Mo2CTx_Mo3AlC2 catalysts
Cite as
Authors
seen 154 times