The electrical conductivity of pristine, La-, and Nb-doped SFM measured in air and hydrogen atmospheres

Description

This dataset consists of an Excel sheet with the result of DC4W method of electrical measurements. The measurements were conducted on pristine strontium ferrite molubdate as well as ones doped with La and Nb. Additionally two samples co-doped with La and Ni/Co were analyzed. Pellets were prepared by high temperature sintering at 1400 deg. C, then cut into rectangles. Platinum electrodes were mounted and samples were put into the measurement cell. Firstly sample were heated up to 900 deg. C in air, then datapoints were collected during cooling. Each temperature was hold for several hours to allow relaxation. Then the gas was switched to inert gas, to rinse the cell before enabling the hydrogen flow. Same procedure was repeated for hydrogen atmosphere.

Dataset file

Electrical_conductivity_012023_SFM_LSFM(10Co, 10Ni)_SFMNb.xlsx

85.8 kB, S3 ETag 7e261446728254652038788bfb195d7e-1, downloads: 6

The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

File details

License:: open in new tab

CC BY

Attribution
File embargo:: 2025-06-15

Details

Year of publication:

2024

Verification date:

2024-01-15

Dataset language:

English

Fields of science:

materials engineering (Engineering and Technology)

DOI:

10.34808/f06g-w664

Funding:

The impact of nanoparticles exsolved from double perovskite on the efficiency of biogas-fueled SOFC

Series:

Verified by:

Gdańsk University of Technology

Keywords

Cite as

Authors

seen 102 times

Search