The morphology of lead-borate glasses and nanocomposites doped with iron oxide

Description

The topography of iron-doped borate glasses and glass-ceramics were studied. Samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 < x < 37 in mol%) were prepared by the conventional melt
quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate and pressed by an another plate to obtain flat
circular samples of 1–2 mm thickness and 20–30 mm in diameter. The quenched pellets were annealed at the temperature of 673 K for 3 h and cooled with the furnace. The microstructure of all samples was determined by means of atomic forcemicroscopy at their fresh fractureswith the use of NT-MDT Ntegra AFM. Detailed information can be found in: http://dx.doi.org/10.1016/j.ssi.2014.01.042

Dataset file

set9.zip

89.4 MB, S3 ETag 43f7abf082bc477b3342a5b58c9f0d5f-1, downloads: 10

The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

download

File details

License:: open in new tab

CC BY

Attribution
Raw data:: Data contained in dataset was not processed.
Software:: Gwyddion

Details

Year of publication:

2014

Verification date:

2021-05-05

Dataset language:

English

Fields of science:

materials engineering (Engineering and Technology)

DOI:

10.34808/hcwb-e504

Verified by:

Gdańsk University of Technology

Keywords

References

publication Electrical properties and structure of lead-borate glass containing iron ions

Cite as

Authors

seen 62 times

Search