The morphology of lead-silicate glasses and nanocomposites doped with iron oxide

Description

The topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573 K and formed into button-shaped samples. Afterwards pellets were
annealed at 673K, cooledwith the furnace and polished to the thickness of about 1mm.
The microstructure of all samples was determined by means of atomic forcemicroscopy at their fresh fractureswith the use of NT-MDT Ntegra AFM. Detailed information can be found in: http://dx.doi.org/10.1016/j.ssi.2013.10.008

Dataset file

set5.zip

48.8 MB, S3 ETag 9ac36337c74924c9fcf73dd00c150978-1, downloads: 14

The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

download

File details

License:: open in new tab

CC BY

Attribution
Raw data:: Data contained in dataset was not processed.
Software:: Gwyddion

Details

Year of publication:

2014

Verification date:

2021-05-05

Dataset language:

English

Fields of science:

materials engineering (Engineering and Technology)

DOI:

10.34808/fexz-v581