The SEM images of Ce0.8La0.2O2 nanocatalyst infiltrated with 10wt.% Ni prepared using soft template method

Description

The dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method and infiltrated to 10wt.% Ni in the catalyst. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate was heated up to 90oC, centrifuged and washed several times. The powders were calcined at 400oC. Powder was single-phase.

The Ni was introduced using nitrate solution (Ni(NO3)2*6H2O)) in water with the addition of beta-cyclodextrin.

Dataset file

Ce0.8La0.2O2 SEM 10wt.%Ni.zip

16.9 MB, S3 ETag 4e9c7321db53bb37bcb171e8cb08dbc1-1, downloads: 47

The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

download

File details

License:: open in new tab

CC BY-NC

Non-commercial
Raw data:: Data contained in dataset was not processed.

Details

Year of publication:

2021

Verification date:

2021-06-10

Creation date:

2020

Dataset language:

English

Fields of science:

materials engineering (Engineering and Technology)

DOI:

10.34808/nm9t-f324

Funding:

Anode catalytic materials for direct internal reforming solid oxide fuel cells (DIR-SOFCs)

Verified by:

Gdańsk University of Technology

Keywords

References

dataset The XRD diffraction patterns of Ce0.8La0.2O2/Ni prepared using soft template method and impregnation

Cite as

Authors

seen 97 times

Search