The XRD diffraction patterns of as-preapred (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials

Description

The (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA) in a molar ratio equal to 2:1 until a white slurry was obtained. The water-based solution was then added to a titanium precursor mixture and stirred at 80C until fully dissolved. After this, the solution was heated to 150C and condensed until gel was obtained. Next, the gel was transferred into an alumina crucible and calcined for 1 h at 400C, then for 1 h at 600C and finally at 1200C for 12 h under an air atmosphere. 

Dataset file

LSCFeT as-prepared.zip
813.0 kB, S3 ETag 0797f003188749cf82faca08e9c24e4b-1, downloads: 1
The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

File details

License:
Creative Commons: by 4.0 open in new tab
CC BY
Attribution
File embargo:
2026-04-30
Raw data:
Data contained in dataset was not processed.

Details

Year of publication:
2024
Verification date:
2024-03-08
Dataset language:
English
Fields of science:
  • materials engineering (Engineering and Technology)
DOI:
DOI ID 10.34808/72a0-9556 open in new tab
Funding:
Verified by:
Gdańsk University of Technology

Keywords

Cite as

seen 91 times