Thermal behavior of VO2/V2O3 nanostructures obtained at 600°C under argon atmosphere

Description

The DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures.  The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 600°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.

Thermogravimetric analysis (TG) and Differential scanning calorimetry (DSC) measurements were carried out under synthetic air atmosphere from 40°C to 650°C (with a heating rate of 15 °C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum (MS). The gases that come out from the samples during heating were monitored by the quadruple mass spectrometer Netzsch QMS 403C Aeolos. The mass spectra were measured for selected m/z from 12 to 44.

Dataset file

Xero600_Ar.zip
164.6 kB, S3 ETag d635a8173117abe02739ff528de81f83-1, downloads: 18
The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5
download file Xero600_Ar.zip

File details

License:
Creative Commons: by 4.0 open in new tab
CC BY
Attribution
Raw data:
Data contained in dataset was not processed.

Details

Year of publication:
2021
Verification date:
2021-07-13
Dataset language:
English
Fields of science:
  • Materials engineering (Engineering and Technology)
DOI:
DOI ID 10.34808/hn25-ja78 open in new tab
Series:
Verified by:
Gdańsk University of Technology

Keywords

References

Cite as

seen 74 times