Wpływ procesu redukcji na właściwości strukturalne i mechaniczne szkieł tlenkowych z grupy (Pb,Bi)-(Si,Ge)-O = Influence of reduction process on the structural and mechanical properties of (Pb,Bi)-(Si,Ge)-O oxide glasses
Abstract
The effect of the reduction process in H2 at 380 °C on the microstructure and elemental composition of a glass Bi0.4Pb0.2Si0.4Ox has been investigated. It has been shown that after reduction a clearly separated top layer with a thickness of approx. 50 µm was formed on the surface of the sample. This layer is depleted of oxygen and has higher electrical conductivity than the interior of the glass. It has also been found that some granules of metallic bismuth with a diameter of tens to hundreds of nanometers were formed on the surface of the glass. Furthermore, depletion of lead was observed in these samples in relation to the initial stoichiometry of the glass prior to trial reduction.
Author (1)
Cite as
Full text
- Publication version
- Accepted or Published Version
- License
- open in new tab
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Published in:
-
Technical Issues
no. 2,
pages 3 - 8,
ISSN: 2392-3954 - Language:
- Polish
- Publication year:
- 2015
- Bibliographic description:
- Bochentyn B.: Wpływ procesu redukcji na właściwości strukturalne i mechaniczne szkieł tlenkowych z grupy (Pb,Bi)-(Si,Ge)-O = Influence of reduction process on the structural and mechanical properties of (Pb,Bi)-(Si,Ge)-O oxide glasses// Technical Issues. -Vol. 2., (2015), s.3-8
- Verified by:
- Gdańsk University of Technology
seen 114 times
Recommended for you
High temperature oxidation behavior of SUS430 SOFC interconnects with Mn-Co spinel coating in air
- C. Jia,
- Y. Wang,
- S. Molin
- + 3 authors
Properties of Composite Oxide Layers on The Ti13Nb13Zr Alloy
- A. Ossowska,
- R. Beutner,
- D. Scharnweber
- + 1 authors