SEM micrographs of vanadium oxide nanostructures obtained by V2O5 recrystallization at 800°C
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of vanadium oxide nanostructures on quartz glass and silicon substrates obtained by recrystallization of V2O5 thin films at 800°C under synthetic air. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials.
-
SEM micrographs of vanadium oxide nanostructures obtained by V2O5 recrystallization at 1200°C
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of vanadium oxide nanostructures on quartz glass and silicon substrates obtained by recrystallization of V2O5 thin films at 1200°C under synthetic air. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials.
-
Electrical measurements of the dewetting of metal thin films
Open Research DataIn situ observations of dewetting of thin films is very complicated. One of the method, that helps to observe it, could be electrical measurements. For experiments, thin gold, silver and gold-silver nanoalloy films were deposited by magnetron sputtering method. Films were deposited on a Corning glass substrates. Samples were measured by four point method...
-
Ni-based compounds in multiwalled graphitic shell for electrocatalytic oxygen evolution reactions
Open Research DataThis study investigates Ni-based compounds (Ni, NiO, Ni3C) coated with a graphitic shell as electrocatalysts for the oxygen evolution reaction (OER). Electron paramagnetic resonance (EPR) and X-ray diffraction (XRD) are employed to identify the presence and contribution of Nickel ions (Ni0, Ni2+, Ni3+) and determine the phase composition. Electrochemical...
-
Ethylene decomposition on TiO2 - UV and Fluorescence lamp
Open Research DataData contain chromatograms recorded during decomposition of ethylene flowing over TiO2 through the quartz tubular shape reactor. TiO2 was coated onto glass plates with dimension of 2cmx2cm, in total 3 plates were used and placed inside reactor. Reactor was irradiated by UV (Special 'TL'E, Philips) or fluorescent (Lumilux, OSRAM) 3 ring-shaped lamps,...
-
The structure of 70(2Bi2O3-V2O5) - 30SrBO7 measured with X-ray diffraction and SEM methods
Open Research DataThe structure changes of 70(2Bi2O3-V2O5)-30SrB4O7 glass occurred during increase in temperature was measured by XRD and SEM.
-
Topography and microstructure of phosphate-iron glasses containing niobium and titanium
Open Research DataThe topography and microstructure of phosphate-iron glasses containing niobium and titanium were investigated by the means of X-ray diffraction (XRD), scanning electron microscopy (SEM). Glass samples of the composition of 35P2O5-30Fe2O3-(35-x)Nb2O5-xTiO2 where x= 0; 7.5 and 15 (in %mol) were prepared by the conventional melt quenching technique. Appropriate...
-
Investigation of the uniformity of TeO2:Eu layer
Open Research DataTeO2 doped by Eu thin films manufactured by magnetron sputtering method were measured by XPS method. Te-Eu mosaic target with diameter of 50.8 mm was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the deposition chamber was below 0.2 Pa and substrate was heated at 200 oC during...
-
The structure of lead-silicate glasses and nanocomposites doped with iron oxide
Open Research DataThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573...
-
The morphology of lead-silicate glasses and nanocomposites doped with iron oxide
Open Research DataThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573...
-
The structure of lead-silicate glasses containing nanocrystallites of iron oxides
Open Research DataThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
The morphology of lead-silicate glasses containing nanocrystallites of iron oxides
Open Research DataThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
Luminescence properties of TeOx thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
Study of the influence of the presence of Dr fimbriae on the adherence of cells of the recombinant Escherichia coli strain: AAEC191A/pACYCpBAD to polystyrene in a dynamic system
Open Research DataThe attachment of bacteria begins the process of surface colonization, called biofilm development, characterized by a number of physicochemical and molecular interactions. Adherence to inert surfaces typically involves nonspecific interactions, whereas adherence to biological surfaces is associated with specific ligand-receptor interactions. In this...
-
Study of the influence of the presence of Dr fimbriae on the adherence of cells of the recombinant Escherichia coli strain: BL21(DE3)/pCC90 to polystyrene in a dynamic system
Open Research DataThe attachment of bacteria begins the process of surface colonization, called biofilm development, characterized by a number of physicochemical and molecular interactions. Adherence to inert surfaces typically involves nonspecific interactions, whereas adherence to biological surfaces is associated with specific ligand-receptor interactions. In this...
-
Study of the influence of the presence of Dr fimbriae on the adherence of cells of the recombinant Escherichia coli strain: BL21(DE3)/pACYCpBAD to polystyrene in a dynamic system
Open Research DataThe attachment of bacteria begins the process of surface colonization, called biofilm development, characterized by a number of physicochemical and molecular interactions. Adherence to inert surfaces typically involves nonspecific interactions, whereas adherence to biological surfaces is associated with specific ligand-receptor interactions. In this...
-
Study of the influence of the presence of Dr fimbriae on the adherence of cells of the recombinant Escherichia coli strain: AAEC191A/pCC90 to polystyrene in a dynamic system
Open Research DataThe attachment of bacteria begins the process of surface colonization, called biofilm development, characterized by a number of physicochemical and molecular interactions. Adherence to inert surfaces typically involves nonspecific interactions, whereas adherence to biological surfaces is associated with specific ligand-receptor interactions. In this...
-
The morphology of lead-borate glasses and nanocomposites doped with iron oxide
Open Research DataThe topography of iron-doped borate glasses and glass-ceramics were studied. Samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 < x < 37 in mol%) were prepared by the conventional meltquenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate...
-
Optical properties of tellurium dioxide thin films
Open Research DataTeO2 and TeO2 doped by Eu thin films manufactured by magnetron sputtering method were measured by optical spectroscopy. Metallic Te target and Te-Eu mosaic target with diameter of 50.8 mm were sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate...
-
Luminescence properties of TeOx-Eu thin films
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Eu thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Tb thin films
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Tb thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Dy thin films
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions....
-
Comparison of XPS spectra of Ag3d for silver nanostructures and bulk material
Open Research DataAg nanostructures were prepared on borosilicate glass (Corning 1737F) and Si substrates. In both cases, the substrateswere cleaned with acetylacetone and then rinsed in ethanol. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The...
-
Luminescence properties of TeOx-Dy thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions....
-
Plasmon resonance in gold-silver nanoalloys
Open Research DataSurface plasmon resonance (SPR) can lead to improve or formation a new linear or nonlinear optical phenomena. Especially it can enhance a light emission from luminescence materials. The presence of metal nanostructures or nanoparticles is necessary to excitation of the SPR. It is well known that gold and silver nanostructures exhibit plasmon resonance...
-
Investigation of plasmon resonance in a silver nanoparticles
Open Research DataSilver nanostructures were prepared on borosilicate glass (Corning 1737F) substrates. Thin Ag films (1–9 nm thickness) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1, and the incident...
-
Luminescence properties of TeOx-Tb thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Tb thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Eu thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Eu thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Kinetics of hexane and cyclohexane biodegradation using Candida subhashii in mineral salt medium in the presence of DES solution
Open Research DataDataset presents results of investigations on kinetics of biodegradation of hexane and cyclohexane in Candida subhashii.
-
Linear and nonlinear impedance of iron containing silicate glasses
Open Research DataThe linear and nonlinear impedance ofglasses doped with iron oxide were measured. Glass samples (50 SiO2-50-xPbO-xFe2O3 in mol%) were prepared by the conventional melt quenching technique. The substrates were powdered in a mortar and melted in Al2O3 crucibles. The melting was conducted in air at 1623K. The melts were poured out on plate heated up to...
-
Topography of barium-vanadate glasses
Open Research DataThe topography of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was performed...
-
Luminescence properties of TeOx-2%Eu1.5%Tb1.5%Dy thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-2%Eu1.5%Tb1.5%Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Luminescence properties of TeOx-2%Eu1.5%Tb1.5%Tm thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-2%Eu1.5%Tb1.5%Tm thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Luminescence properties of TeOx-1%Eu1.5%Tb2.5%Dy thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-1%Eu1.5%Tb2.5%Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Electrical properties of silicate-lead glasses containing nanostructures of iron oxides.
Open Research DataElectrical properties of silicate-lead glasses doped with different content of iron oxide was studied. The set of glass samples were prepared with the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in...
-
Dielectric properties of barium-vanadate glasses
Open Research DataThe linear impedance of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was...
-
The topography of as-quenched and heat treated 58(2Bi2O3-V2O5)-42SrB4O7 glasses measured with confocal microscope
Open Research DataThe topography of as-quenched and heat treated 58(2Bi2O3-V2O5)-42SrB4O7 glasses measured with confocal microscope.
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Open Research DataThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...
-
The PolarScreen™ Estrogen Receptor Competitor Assays for determination of estradiol equivalent concentrations (EEQs) in sewage and drinking water samples.
Open Research DataMunicipal waste waters are one of the main sources of estrogenic compounds in aquatic environments. Feminization of fish downstream of Waste Water Treatment Plants (WWTPs) discharges has been observed worldwide. Some estrogenic chemicals, particularly steroid estrogens, are known to cause disruption of the endocrine system of fishes and abnormalities...
-
The values of Permutation Entropy for individuals with Normal Sinus Rhythm
Open Research DataThe dataset consists of calculated values of entropy of 75 000 intervals between consecutive heartbeats (RR intervals) for 54 patients with normal sinus rhythm (NSR). The original data were taken from PhysioNet Normal Sinus Rhythm RR Interval Database (cf. Goldberger A., Amaral L., Glass L., Hausdorff J., Ivanov P.C., Mark R., Mietus J.E., Moody G.B.,...
-
The values of Permutation Entropy for patients with Congestive Heart Failure
Open Research DataThe dataset consists of calculated values of entropy of 75 000 intervals between consecutive heartbeats (RR intervals) for 29 patients with congestive heart failure (CHF). The original data were taken from PhysioNet Congestive Heart Failure RR Interval Database (cf. Goldberger A., Amaral L., Glass L., Hausdorff J., Ivanov P.C., Mark R., Mietus J.E.,...
-
The morphology of as-quenched and heat treated 58(2Bi2O3-V2O5)-42SrB4O7 glasses measured with AFM
Open Research DataThe morphology of as-quenched and heat treated 58(2Bi2O3-V2O5)-42SrB4O7 glasses was measured with the use of atomic force microscope.
-
The values of Block Entropy for individuals with Normal Sinus Rhythm
Open Research DataThe dataset consists of calculated values of entropy of 75 000 intervals between consecutive heartbeats (RR intervals) for 54 patients with normal sinus rhythm (NSR). The original data were taken from PhysioNet Normal Sinus Rhythm RR Interval Database (cf. Goldberger A., Amaral L., Glass L., Hausdorff J., Ivanov P.C., Mark R., Mietus J.E., Moody G.B.,...
-
Topography of iron-phosphate glasses doped with niobium and titanium tested by confocal microscope
Open Research DataThe topography of phosphate-iron glasses containing niobium and titanium were investigated with the use of confocal miscroscope. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5, 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 and 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents...
-
The values of Block Entropy for patients with Congestive Heart Failure
Open Research DataThe dataset consists of calculated values of entropy of 75 000 intervals between consecutive heartbeats (RR intervals) for 29 patients with congestive heart failure (CHF). The original data were taken from PhysioNet Congestive Heart Failure RR Interval Database (cf. Goldberger A., Amaral L., Glass L., Hausdorff J., Ivanov P.C., Mark R., Mietus J.E.,...
-
Linear impedance of 35P2O5-30Fe2O3-20Nb2O5-15TiO2
Open Research DataThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...
-
Linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Open Research DataThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and...
-
Linear impedance of 35P2O5-30Fe2O3-35Nb2O5
Open Research DataThe electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2 (≥99.9%, anatase...
-
Scanning electrochemical micrographs of poly(lactic acid) 3D printed electrodes ablated by femtosecond laser
Open Research DataThe dataset contains the scanning electrochemical micrographs of the femtosecond laser (FSL) ablation at the surface of commercially available carbon black-filled poly(lactic acid) 3D printed electrode. The process is used for the increase of the charge transfer of this electrode in electrochemical studies.
-
Microstructure of barium-vanadate glasses
Open Research DataThe structure of barium-vanadate glasses was measured by SEM and XRD techniques. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar....