The topography of as-quenched and heat treated 58(2Bi2O3-V2O5)-42SrB4O7 glasses measured with confocal microscope
Open Research DataThe topography of as-quenched and heat treated 58(2Bi2O3-V2O5)-42SrB4O7 glasses measured with confocal microscope.
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Open Research DataThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...
-
The PolarScreen™ Estrogen Receptor Competitor Assays for determination of estradiol equivalent concentrations (EEQs) in sewage and drinking water samples.
Open Research DataMunicipal waste waters are one of the main sources of estrogenic compounds in aquatic environments. Feminization of fish downstream of Waste Water Treatment Plants (WWTPs) discharges has been observed worldwide. Some estrogenic chemicals, particularly steroid estrogens, are known to cause disruption of the endocrine system of fishes and abnormalities...
-
The values of Permutation Entropy for individuals with Normal Sinus Rhythm
Open Research DataThe dataset consists of calculated values of entropy of 75 000 intervals between consecutive heartbeats (RR intervals) for 54 patients with normal sinus rhythm (NSR). The original data were taken from PhysioNet Normal Sinus Rhythm RR Interval Database (cf. Goldberger A., Amaral L., Glass L., Hausdorff J., Ivanov P.C., Mark R., Mietus J.E., Moody G.B.,...
-
The values of Permutation Entropy for patients with Congestive Heart Failure
Open Research DataThe dataset consists of calculated values of entropy of 75 000 intervals between consecutive heartbeats (RR intervals) for 29 patients with congestive heart failure (CHF). The original data were taken from PhysioNet Congestive Heart Failure RR Interval Database (cf. Goldberger A., Amaral L., Glass L., Hausdorff J., Ivanov P.C., Mark R., Mietus J.E.,...
-
The morphology of as-quenched and heat treated 58(2Bi2O3-V2O5)-42SrB4O7 glasses measured with AFM
Open Research DataThe morphology of as-quenched and heat treated 58(2Bi2O3-V2O5)-42SrB4O7 glasses was measured with the use of atomic force microscope.
-
The values of Block Entropy for individuals with Normal Sinus Rhythm
Open Research DataThe dataset consists of calculated values of entropy of 75 000 intervals between consecutive heartbeats (RR intervals) for 54 patients with normal sinus rhythm (NSR). The original data were taken from PhysioNet Normal Sinus Rhythm RR Interval Database (cf. Goldberger A., Amaral L., Glass L., Hausdorff J., Ivanov P.C., Mark R., Mietus J.E., Moody G.B.,...
-
Topography of iron-phosphate glasses doped with niobium and titanium tested by confocal microscope
Open Research DataThe topography of phosphate-iron glasses containing niobium and titanium were investigated with the use of confocal miscroscope. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5, 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 and 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents...
-
The values of Block Entropy for patients with Congestive Heart Failure
Open Research DataThe dataset consists of calculated values of entropy of 75 000 intervals between consecutive heartbeats (RR intervals) for 29 patients with congestive heart failure (CHF). The original data were taken from PhysioNet Congestive Heart Failure RR Interval Database (cf. Goldberger A., Amaral L., Glass L., Hausdorff J., Ivanov P.C., Mark R., Mietus J.E.,...
-
Linear impedance of 35P2O5-30Fe2O3-20Nb2O5-15TiO2
Open Research DataThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...
-
Linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Open Research DataThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and...
-
Linear impedance of 35P2O5-30Fe2O3-35Nb2O5
Open Research DataThe electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2 (≥99.9%, anatase...
-
Scanning electrochemical micrographs of poly(lactic acid) 3D printed electrodes ablated by femtosecond laser
Open Research DataThe dataset contains the scanning electrochemical micrographs of the femtosecond laser (FSL) ablation at the surface of commercially available carbon black-filled poly(lactic acid) 3D printed electrode. The process is used for the increase of the charge transfer of this electrode in electrochemical studies.
-
Microstructure of barium-vanadate glasses
Open Research DataThe structure of barium-vanadate glasses was measured by SEM and XRD techniques. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar....
-
High temperature linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Open Research DataThe high temperature electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
High temperature linear impedance of 35P2O5-30Fe2O3-25Nb2O5-15TiO2
Open Research DataThe high temperature electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%,...
-
High temperature linear impedance of 35P2O5-30Fe2O3-35Nb2O5
Open Research DataThe high temperature electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...
-
Surface modifcation of PMMA polymer detected by XPS
Open Research DataIn order to obtain the experimental specimens, four PMMA/PC61BM samples with the following mass proportions were prepared: 10%, 20%, 30%, and 40%. In addition, as a reference, a PMMA sample without PC61BM was prepared as well. For the fabrication process, PC61BM 99.5% (Solenne BV), chloroform HPLC (Sigma Aldrich), and PMMA (commercially available...
-
The topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with confocal microscope
Open Research DataThe topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with confocal microscope.
-
The topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with AFM
Open Research DataThe topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with AFM.
-
Plasmon resonance in a TiO2-Au NPs structures
Open Research DataInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...