Search
Filters
total: 117
filtered: 32
-
Catalog
Chosen catalog filters
Search results for: INTERGRANULAR CORROSION, NDT, EMAT, ULTRASONIC TESTING
-
The AFM micrographs of austenitic stainless steel subjected to sensitization for intergranular corrosion
Open Research DataThe dataset contains atomic force microscopy (AFM) maps of topographic images of austenitic steel samples subjected to sensitization to the process of intergranular corrosion. Precipitations of carbides as well as other intermetallic phases can be observed and detected before the fragments of structures sensitized by improper thermal treatment are exposed...
-
The SEM micrographs of the cavitation erosion-corrosion process of selected copper alloys degradation
Open Research DataThe dataset contains Scanning Electron Micrographs of CuZn40Mn3Fe brass compared with Superston and Novoston bronze after cavitation erosion-corrosion exposure using a vibratory transducer (in accordance with ASTM G32). The micrographs compare the topography of samples subjected cavitation erosion in 3% NaCl at room temperature, leading to the surface...
-
The SEM micrographs of the synergistic action between cavitation erosion and pitting corrosion on stainless steel 304
Open Research DataThe dataset contains Scanning Electron Micrographs of stainless steel AISI304 samples made after cavitation erosion-corrosion exposure using a vibratory transducer (in accordance with ASTM G32). The micrographs compare the topography of samples subjected to either cavitation erosion (in deionized water), pitting corrosion (in 8% FeCl3 solution, without...
-
Scanning electron microscopy studies of the weld decay on SS 304 of water supply pipeline
Open Research DataThis dataset contains micrographs made with scanning electron microscope (SEM) Hitachi S-3400N, of the weld decay for water supply system pipelines made of AISI 304 stainless steel. Within the dataset one can see the different corrosion mechanisms. The micrographs were made after the Strauss test (excluding pictures labeled as pits_in_HAZ, done without...
-
Thermographic images during testing measuring instrument boards
Open Research DataThe dataset presents thermografic images acquired during testing the prototype of measuring instrument for resistiometric corrosion monitoring. The testing was performed in the room temperature. VIGOcam v50 thermal imaging camera (VIGO System S.A., Ozarow Mazowiecki, Poland) was used for taking the pictures. These pictures were used as preliminary tests...
-
SEM micrographs of the topography of Cu-Sn-TiO2 nanocomposite coatings
Open Research DataThe dataset contains the scanning electron microscopy (SEM) micrographs of nanocomposite Cu-Sn-TiO2 coatings electrodeposited from oxalic acid bath containing Cu and Sn salts as well as TiO2 nanoparticles under various treatments: mechanical stirring, ultrasonic or none. The details of the electrodeposition process are presented in the readme file attached...
-
The exemplary Kelvin probe microscopy studies of sensitized austenitic stainless steels
Open Research DataThe dataset summarizes the results of imaging the surface potential distribution using the Kelvin probe scanning technique. Due to the fact that the potential measured in this way is proportional to the electrochemical potential of metals or intermetallic phases, it is possible to assess the nobility differences of various alloy components. In the case...
-
Austenitic stainless steel sensitization
Open Research DataHigh-alloy steels, thanks to their composition and content of appropriate alloying additives, are characterized by increased resistance to many corrosive environments. However, this is due to the increased sensitivity of the described construction materials to specific environmental conditions during their use. An example may be the increased susceptibility...
-
Imaging of morphological and physicochemical changes occuring in the structure of austenitic steel due to the thermal sensitization
Open Research DataIn polycrystalline materials, grain boundaries are always where phenomena such as surface diffusion, sedimentation and corrosion occur. They have a significant impact on the macroscopic properties of the construction material [1]. In addition to inhomogeneities such as manganese sulphide inclusions formed during the metallurgical process, interfacial...
-
SEM micrographs of cavitation erosion-corrosion of aluminium alloy 2024 with anodic polarization
Open Research DataThe dataset contains Scanning Electron Micrographs of aluminium alloy 2024 samples made after cavitation erosion-corrosion exposure using a vibratory transducer (in accordance with ASTM G32). The experiment duration was 240 min, with cyclic cavitation exposure in on/off cycles 30s:30s. The electrolyte was 0.1 M KNO3 solution. Some samples were anodically...
-
The XPS studies revealing the surface chemistry of Cu-Sn-TiO2 nanocomposite coatings
Open Research DataThe dataset contains the X-Ray Photoelectron Spectroscopy (XPS) data of nanocomposite Cu-Sn-TiO2 coatings electrodeposited from oxalic acid bath containing Cu and Sn salts as well as TiO2 nanoparticles under various treatments: mechanical stirring, ultrasonic or none. The details of the electrodeposition process are presented in the descriptor file...
-
Microscopic examination of CuNiFeR pipeline
Open Research DataCopper and nickel alloys called cunifers (Cu, Ni, Fe and R – rest of alloy elements) have found wide application in the production of ship pipeline components in contact with sea water, such as, for example, the main engine cooling system. These alloys are characterized by a very high corrosion resistance, which is ensured by appropriately carried out...
-
Macroscopic examination of CuNiFeR pipeline
Open Research DataCopper and nickel alloys called cunifers (Cu, Ni, Fe and R – rest of alloy elements) have found wide application in the production of ship pipeline components in contact with sea water, such as, for example, the main engine cooling system. These alloys are characterized by a very high corrosion resistance, which is ensured by appropriately carried out...
-
Tensile test of part of CuNiFeR pipeline
Open Research DataCopper and nickel alloys called cunifers (Cu, Ni, Fe and R – rest of alloy elements) have found wide application in the production of ship pipeline components in contact with sea water, such as, for example, the main engine cooling system. These alloys are characterized by a very high corrosion resistance, which is ensured by appropriately carried out...
-
Ultrasonic wave propagation and digital image correlation measurements of steel bars under 3-point bending
Open Research DataThe DataSet contains the results of the mechanical behaviour of a bar under a 3-point bending test. The bar was made of steel and had a cross-section of 5.96 × 5.96 mm2 and a length of 200 mm. The three-point bending test was performed using a Zwick/Roell Z10 universal testing machine (UTM), with a distance between supports of 12 cm. The parameters...
-
Wave propagation signals in concrete beams under 3-point bending
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete beams with dimensions 40 x 40 x 160 cm3under the 3-point bending. The beams were made of concrete with the following ingredients: CEM I 42.5R (450 kg/m3), water (177 kg/m3), sand 0-2 (675 kg/m3) and gravel 2-8 (675 kg/m3). The bending test was performed using a Zwick/Roell Z10...
-
Straightening of ship hull structure made of 316L stainless steel - tensile test of water cooled materia
Open Research DataThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - tensile test of reference material materia (transverse direction)
Open Research DataThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - tensile test of reference material materia (longitudinal direction)
Open Research DataThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - microstructure of naturally colled material
Open Research DataThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - microstructure of water cooled material
Open Research DataThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - microstructure of reference material
Open Research DataThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - tensile test of naturally cooled material
Open Research DataThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-002)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-Con)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-004)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-006)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
PA32 aluminum alloy - tensile properties
Open Research DataIn addition to steel, aluminium alloys are the main building material used in the shipbuilding industry. Due to its undoubted advantages, such as low density (nearly three times lower than in the case of steel for shipbuilding) and high corrosion resistance, it is often used for hulls of yachts and small vessels as well as superstructures. For safety...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #3)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #1)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #4)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #2)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...