dr inż. Tadeusz Miruszewski
-
The electrical conductivity relaxation curve of the SrxTi0.30Fe0.70O3 (x=0.90 and 1.00) at 700 °C
Open Research DataIn this dataset are presented exemplary curves used for analysis of the electrical conductivity relaxation (ECR) mesurement of the SrxTi0.30Fe0.70O3 (x=0.90, 1.00) materials. The applied measuring temperature were 700 °C. Studies were performed in a small tube furnace (internal diameter ~20 mm) with 64 cm3 gas volume. During the four-point single frequency...
-
Chemical oxygen surface exchange coefficient (k*) of the SrxTi0.30Fe0.70O3 (x=0.90, 0.95 and 1.00) at different temperatures
Open Research DataIn this dataset are presented k* values designated based on the analysis of the electrical conductivity relaxation (ECR) mesurement of the SrxTi0.30Fe0.70O3 (x=0.90, 0.95, 1.00) materials. The applied temperatures were 800 °C, 750 °C, 700 °C, 650 °C, and 600 °C. Studies were performed in a small tube furnace (internal diameter ~20 mm) with 64 cm3 gas...
-
Chemical diffusion coefficient of oxygen (D*) of the SrxTi0.30Fe0.70O3 (x=0.90, 0.95 and 1.00) at different temperatures
Open Research DataIn this dataset are presented D* values designated based on the electrical conductivity relaxation (ECR) mesurement of the SrxTi0.30Fe0.70O3 (x=0.90, 0.95, 1.00) materials. The applied temperatures were 800 °C, 750 °C, 700 °C, 650 °C, and 600 °C. Studies were performed in a small tube furnace (internal diameter ~20 mm) with 64 cm3 gas volume. During...
-
Impact of strontium non-stoichiometry of SrxTi0.3Fe0.7O3-δ
Open Research DataThis dataset contains results of the research on the basis of which the Figures presented in the manuscript entitled "Impact of strontium non-stoichiometry of SrxTi0.3Fe0.7O3-δ on structural, electrical, and electrochemical properties for potential oxygen electrode of intermediate temperature Solid Oxide Cells" were prepared. A detailed description...
seria: Data used in article "Water uptake kinetics and electrical transport in BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Tb, Pr, Fe) protonic conductors" liczba: 3
expand collapse-
Electrical conductivity relaxation measurements - oxidation and reduction of BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Open Research DataThe dataset consists of 2 main catalogs: measurements performed for oxidation/reduction in dry conditions and in humid conditions. For Electrical Conductivity Relaxation (ECR) measurements, platinum reversible electrodes were applied in a four-probe arrangement and the sample was measured in the ProboStat™ measurement system. The ECR measurements were...
-
Electrical conductivity relaxation measurements - water uptake of BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Open Research DataFor Electrical Conductivity Relaxation (ECR) measurements, platinum reversible electrodes were applied in a four-probe arrangement and the BaCe0.6Zr0.2Y0.1Tb0.1O3-δ sample was measured in the ProboStat™ measurement system. The ECR measurements were performed in air in the temperature range of 450-800 ℃ after switching water partial pressure between...
-
Electrochemical impedance spectroscopy measurements - conductivity vs. temperature and conductivity vs. oxygen partial pressure - BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Open Research DataThe dataset consists of two main catalogs consisting of measurement data: of the electrical conductivity of the BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) sample as a function of temperature and of the electrical conductivity as a function of oxygen partial pressure (pO2). Measurements as a function of temperature were carried out in dry and wet air (pH2O ~...
seria: Electrochemical properties of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrodes liczba: 1
expand collapse-
X-ray diffractometry results of the Sr0.86Ti0.65Fe0.35O3 powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.86Ti0.65Fe0.35O3-d (STF35) powder. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. It confirms the formation of the cubic perovskite oxide phase. Calculated average lattice constant is a 3.90882(1) Å, with Goodness of Fit...
-
Changes on the Surface of the SiO2/C Composite, Leading to the Formation of Conductive Carbon Structures with Complex Nature of DC Conductivity
Open Research DataChanges on the Surface of the SiO2/C Composite, Leading to the Formation of Conductive Carbon Structures with Complex Nature of DC Conductivity