XRD patterns of MXenes catalysts
Open Research DataData contain results from XRD measurements of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios....
-
SEM images of MXene catalysts
Open Research DataData contain results SEM measurements of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios. MAX...
-
TEM, EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures.
Open Research DataData consists of raw TEM/EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures. Additional TEM images and optical microscope images of silica shells were included.
-
X-ray diffraction (XRD) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Open Research DataData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
X-ray diffraction (XRD) of silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Open Research DataData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
TG analyses - content of SiO2 and TiO2 in polystyrene
Open Research DataTG analyses were performed for polystyrene spheres coating by SiO2 and then coating by SiO2-TiO2. Thermal analyses of polystyrene spheres only were also performed. The content of inorganic remaining was used for calculation the quantity of coating SiO2 and TiO2 in the polystyrene spheres.
-
TG-hydroxyl groups in TiO2-P25
Open Research DataTG analyses were performed for powdered TiO2 - commercial P25 sample, which was heat-treated from room temperature to 500 C in the nitrogen atmosphere. Mass loss at lower temperature such as 120 C was related to the physisorbed water, and that one occurring at 500 C to the chemisorbed hydroxyl groups.
-
TiO2-potential zeta in water
Open Research DataData contain results from measurements of zeta potential for powdered TiO2 in a diluted aqueous solution. The measurements were performed in Zetasizer Nano ZS analyser.
-
Photocatalytic decomposition of ethylene on the TiO2-polystyrene spheres
Open Research DataData contain results from the measurements of the photocatalytic decomposition of ethylene under UV irradiation with using TiO2 coating on the expanded polystyrene spheres (EPS). EPS-SiO2-TiO2 and EPS-TiO2 were used as the photocatalytic beds in the fluidized bed reactor. Both, stationary and fluidized beds were tested. The comparison of ethylene decomposition...
-
TiO2-TG analyses -OH groups
Open Research DataTG analyses of TiO2 were performed under nitrogen flow to monitor desorption of hydroxyl groups. Physisorbed weak-bonded hydroxyl groups were desorbed totally at around 120oC, whereas chemisorbed ones at around 500oC. The mass loss at these temperatures was used as concentration of hydroxyl groups on TiO2 surface. The amount of analysed TiO2 was 10...
-
TiO2-zeta potential
Open Research DataData contain results from the measurements of zeta potential of TiO2 versus pH. Data are saved as original files and in the format of Excel file. measurements were perfomed in Zetasizer Nano ZS with using Multi-Purpose Titrator MPT-2.
-
Ethylene decomposition on TiO2 - UV and Fluorescence lamp
Open Research DataData contain chromatograms recorded during decomposition of ethylene flowing over TiO2 through the quartz tubular shape reactor. TiO2 was coated onto glass plates with dimension of 2cmx2cm, in total 3 plates were used and placed inside reactor. Reactor was irradiated by UV (Special 'TL'E, Philips) or fluorescent (Lumilux, OSRAM) 3 ring-shaped lamps,...
-
Ethylene decomposition on TiO2 under UV
Open Research DataData contain chromatograms recorded during decomposition of ethylene over TiO2 in a flow reactor under UV irradiation. Semilac UV lamp with total power of 72 W was used as a source of UV light. Chromatograms were recorded in Trace GC Ultra chromatograph equipped in FID detector. Sampling was realised via the dosing sample loop. TiO2 was coated on the...
-
FTIR in situ - ethylene decomposition on TiO2
Open Research DataThese data contain FTIR spectra recorded in FTIR spectrometer Nicolet iS50 coupled with High Temperature Chamber "The Praying Mantis". These spectra were measured for TiO2 irradiated by UV and under flowing of ethylene gas diluted in air. FTIR spectra were measured in situ during the photocatalytic process of ethylene decomposition. In order to identify...
-
UV-Vis-DR-TiO2 heated at 400-600oC in Ar or H2
Open Research DataThese data contain UV-Vis/DR spectra of TiO2 heated at 400-600oC in Ar or H2. Transformation of spectra to Kubelka-Munk function was performed together with determination of band gap.
-
FTIR-TiO2 heated at 400-600oC in Ar or H2
Open Research DataData contain FTIR diffuse eflectance spectra of TiO2, which was heat-treated at 400-600oC in Ar or H2. Hydrogen reduced TiO2 revealed new bands due to the adsorption of some species on the titania oxygen vacancy sites.