Ionic thermoelectric effect in Cu2-δSe during phase transition
PublikacjaThe ionic Seebeck coefficient was studied in copper selenide with Cu1.99Se, Cu1.95Se and Cu1.8Se stoichiometry which was synthesized with a melt crystallization method. To measure the ionic Seebeck coefficient of copper ions, 0.15C6H12N4CH3I + 0.85CuI solid-state electrolyte was prepared. Electrolyte layers were pressed with copper selenide powder into a sandwich-like structure. At the temperature of 410 K, the materials have ionic...
Rok 2022
-
Pyrolysis of RDF and Catalytic Decomposition of the Produced Tar in a Char Bed Secondary Reactor as an Efficient Source of Syngas
PublikacjaOne of the technical limitations of refuse-derived fuel (RDF) pyrolysis is the high content of tar in its gas products. In order to resolve this problem, a two-stage RDF pyrolysis with a catalyst based on char from RDF pyrolysis is proposed. This paper presents the results of municipal waste pyrolysis beginning in an oven heated to 480 °C and ending with catalytic tar cracking carried out in the temperature range from 800 to 1000...
Rok 2021
-
Kinetic analysis of the reduction of a ternary system of Bi, Sb and Te oxides by hydrogen for BiSbTe3 synthesis
PublikacjaReduction in a hydrogen atmosphere of Bi2O3, Sb2O3 and TeO2 mixes oxides for the synthesis of BiSbTe3 was analysed. The reduction reactions of Sb2O3 and Sb2O4 oxides, as well as Bi2O3+Sb2O3 and Sb2O3+3TeO2 mix- tures, were also evaluated. The reduction of Sb2O4 is investigated for the first time. The reactions of the mixed oxides systems also were not the subject of research so far despite being used for synthesis of the (Bi,Sb)2Te3...
-
Structure and thermoelectric properties of nickel-doped copper selenide synthesised in a hydrogen atmosphere
PublikacjaNickel-doped copper selenide—Cu2-xNixSe (x = 0; 0.01; 0.02; 0.03)—materials with high thermoelectric properties were synthesised through reduction of reagents in hydrogen. The impact of the nickel content on both the microstructure and thermoelectric properties was examined. The nickel-doped samples’ microstructure differed significantly from pristine copper selenide. Besides Cu2Se, copper precipitations were present in the materials....
-
The unstable thermoelectric effect in non-stoichiometric Cu2Se during the non-equilibrium phase transition
PublikacjaThe superionic α ↔ β phase transition in Cu1.96Se thermoelectric material is investigated by means of thermal analysis (DSC) and measurements of Seebeck coefficient and electrical conductivity. Results of the DSC measurements with 1–10 K/min heating and cooling rates show that the material is close to the equilibrium phase composition during the transformation. However, the kinetic limitation of the process exists, which is indicated...
Rok 2020
-
A study of the kinetics of bismuth telluride synthesis by an oxide reduction method
PublikacjaThe kinetics of a reduction of bismuth and tellurium oxides in a hydrogen atmosphere, leading to the formation of thermoelectric bismuth telluride is investigated. The evaluation of the reaction kinetics was based on a thermogravimetric analysis performed in non-isothermal conditions. A non-parametric analysis method and the Friedman method were used for the evaluation of the data. Additionally, for a better understanding of the...
-
New synthesis route of highly porous InxCo4Sb12 with strongly reduced thermal conductivity
PublikacjaHighly porous, In-filled CoSb3 skutterudite materials with an attractive thermoelectric figure of merit (ZT * 1) and corresponding dense samples were fabricated through the cost-effective method of reduction in oxides in dry hydrogen and the pulsed electric current sintering (PECS) method, respectively. The reduction process was described in detail using in situ thermogravimetric analysis of Co2O3, Sb2O3 and In(NO3)35H2O separately...
Rok 2018
-
A study of a reduction of a micro- and nanometric bismuth oxide in hydrogen atmosphere
PublikacjaA reduction of bismuth oxide in hydrogen atmosphere was investigated. The reaction was performed with a material in various structural forms: powder: with micrometric grains, powder with nanometric grains and powder pressed into pellets. The process was performed in both isothermal and non-isothermal conditions. An activation energy of the reaction calculated with Friedman method was found to be about 85 kJ/mol for the reduction...
-
Structure and thermoelectric properties of bismuth telluride—Carbon composites
PublikacjaCarbon nanotubes and amorphous carbon have been introduced into a bismuth telluride matrix (0.15 and 0.30 wt.% ratio) to investigate the influence of the carbon on the composite’s thermoelectric properties. Composites with well-dispersed additives have been obtained by sonication and ball-milling methodology. Carbon nanotubes and an amorphous carbon addition led to a decrease in electric conductivity from 1120 S/cm to 77 S/cm....
Rok 2017
-
Oxygen biosensor based on carbon nanotubes directly grown on graphitic substrate
PublikacjaFilms of carbon nanotubes were synthesized on the graphitic substrates by CVD method in the presence of catalyst. Two different catalysts were used, that is nickel and iron, supported on graphitic substrates. The as-obtained nanotubes were analyzed by SEM imaging with EDX and Raman spectroscopy. The results revealed their multi-walled morphology. Free radical reaction was carried out in order to chemically functionalize synthesized...
-
Structure and thermoelectric properties of Cs-Bi-Te alloys fabricated by different routes of reduction of oxide reagents
PublikacjaCesium-bismuth-telluride polycrystalline materials were fabricated using a cost-effective method based on a reduction of oxide reagents, leading to a production of a material with good thermoelectric properties. Several samples with various initial stoichiometry were prepared by melting of oxide powders at 1050 °C, quenching, milling to powders and then reducing in pure hydrogen at 400 °C. Another concept was to obtain the CsBi4Te6...
Rok 2016
-
Kompozyty termoelektryczne z nanostrukturami węglowymi
PublikacjaJedną z badanych możliwości poprawy własności materiałów termoelektrycznych jest wytwarzanie kompozytów zawierających nanostrukturalne formy węgla. Opisano najważniejsze wnioski z doniesień naukowych nad takimi materiałami. Oczekuje się, że w wyniku rozpraszania na granicach węgiel - materiał termoelektryczny nastąpi rozpraszanie prowadzące do zmniejszenia przewodności cieplnej. Jednocześnie obserwuje się zmniejszenie przewodności...
Rok 2014
-
Correlation between structural and electrical properties in highly porous (Y,Sr)(Ti,Nb)O3-delta SOFC anodes
PublikacjaIn order to find a relationship between structural and electrical properties, niobium and yttrium doped SrTiO3 ceramics were prepared via solid-state reaction. The samples were sintered in hydrogen and air conditions. The samples were also fabricated with a pore-former to obtain highly porous specimens. The electrical properties of Nb-doped SrTiO3 samples and yttrium and niobium co-doped SrTiO3 were compared. The comparable electrical...