Scanning electrochemical micrographs of poly(lactic acid) 3D printed electrodes ablated by femtosecond laser - Open Research Data - MOST Wiedzy

Wyszukiwarka

Scanning electrochemical micrographs of poly(lactic acid) 3D printed electrodes ablated by femtosecond laser

Opis

The dataset contains the scanning electrochemical micrographs of the femtosecond laser (FSL) ablation at the surface of commercially available carbon black-filled poly(lactic acid) 3D printed electrode. The process is used for the increase of the charge transfer of this electrode in electrochemical studies.

The FSL pulse frequency was set to 200 kHz corresponding to a maximal pulse energy of 20.1 µJ. The laser beam was focused on the sample surface to a spot of 25 µm diameter.

100 µm diameter inlaid disk Pt microelectrode, acting as the SECM tip (working electrode), was obtained by sealing a 0.1 mm diameter Pt wire into borosilicate glass capillaries using a PC-10 micropipette puller. A 0.5 mm diameter Pt wire and Ag|AgCl|KCl(3 M) were used as the counter and reference electrodes, respectively. The sample with laser-ablated lines was mounted in the bottom of a custom-made Teflon SECM cell so that the SECM scanning area covered both the ablated lines and the intact sample surface. Constant height imaging was performed with the unbiased sample in 0.8 mM of ferrocenemethanol containing 0.1 M KCl as a supporting electrolyte. The tip was polarised at +0.5 V vs. Ag|AgCl to assure diffusion-limited electrooxidation of the ferrocenemethanol. The tip-to-sample distance was adjusted to 50 µm (normalised distance d/rT = 1).

The selected micrographs were utilized when preparing the manuscript published in Electrochimica Acta: 10.1016/j.electacta.2022.140288

Plik z danymi badawczymi

SECM_raw.zip
169.9 kB, S3 ETag 8dddc75ce47620a92cb0dcb75650032f-1, pobrań: 58
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
pobierz plik SECM_raw.zip

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:
2022
Data zatwierdzenia:
2023-01-30
Język danych badawczych:
angielski
Dyscypliny:
  • nauki chemiczne (Dziedzina nauk ścisłych i przyrodniczych)
DOI:
Identyfikator DOI 10.34808/99y7-wt38 otwiera się w nowej karcie
Finansowanie:
Seria:
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

Cytuj jako

wyświetlono 129 razy