The SEM micrographs of the cavitation erosion-corrosion process of selected copper alloys degradation

Opis

The dataset contains Scanning Electron Micrographs of CuZn40Mn3Fe brass compared with Superston and Novoston bronze after cavitation erosion-corrosion exposure using a vibratory transducer (in accordance with ASTM G32). The micrographs compare the topography of samples subjected cavitation erosion in 3% NaCl at room temperature, leading to the surface deformation combined with intergranular corrosion. The micrographs were taken after various exposure duration between 10 and 240 min, labeled accordingly, with cyclic cavitation exposure in on/off cycles 60s:60s. The samples were mounted directly underneath the ultrasonic transducer. More details on the experiment are to be found in: 10.1016/j.electacta.2016.01.216

Plik z danymi badawczymi

SEM.Cu.zip

114.0 MB, S3 ETag e7793f8fc802a9d7d932ef936e0fc7aa-1, pobrań: 71

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2016

Data zatwierdzenia:

2021-04-28

Język danych badawczych:

angielski

Dyscypliny:

nauki chemiczne (Dziedzina nauk ścisłych i przyrodniczych)
inżynieria mechaniczna (Dziedzina nauk inżynieryjno-technicznych)
inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/vncn-rk05

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja Instantaneous impedance monitoring of synergistic effect between cavitation erosion and corrosion processes

Cytuj jako

Autorzy

wyświetlono 127 razy

Wyszukiwarka