Application of Electrochemical Impedance Spectroscopy to evaluate cathodically protected coated steel in seawater
Abstrakt
Two types of organic coated carbon steel (S235JR2 grade) electrodes were exposed to artificial seawater environment. One prepared type was defect free while the other one had an intentionally introduced φ0,5 cm coating defect. Both kinds of samples were polarized during the exposure to four potentials corresponding to four different cathodic protection levels. Evolution of their EIS spectra is presented in this paper. Results obtained in the experiment indicate that protective organic coating condition could be estimated and monitored in time based on EIS investigations. If a sample is defected EIS allows a recognition of overprotected and unprotected sample. Distinguishing a fully protected sample from partially protected sample based on EIS was troublesome.
Cytowania
-
5
CrossRef
-
0
Web of Science
-
5
Scopus
Autorzy (3)
Cytuj jako
Pełna treść
- Wersja publikacji
- Submitted Version
- Licencja
- otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
CONSTRUCTION AND BUILDING MATERIALS
nr 181,
strony 721 - 726,
ISSN: 0950-0618 - Język:
- angielski
- Rok wydania:
- 2018
- Opis bibliograficzny:
- Narożny M., Żakowski K., Darowicki K.: Application of Electrochemical Impedance Spectroscopy to evaluate cathodically protected coated steel in seawater// CONSTRUCTION AND BUILDING MATERIALS. -Vol. 181, (2018), s.721-726
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.conbuildmat.2018.06.033
- Bibliografia: test
-
- Z. W. Wicks Jr., F. N. Jones, S. P. Pappas, D. A. Wicks. Organic Coatings: Science and Technology. s.l. otwiera się w nowej karcie
- P. A. Sørensen, S. Kiil , K. Dam-Johansen, C. E. Weinell, Anticorrosive coatings: a review, J. Coat. otwiera się w nowej karcie
- Technol. Res. 6 (2009) 135-176. otwiera się w nowej karcie
- M. Zubielewicz, W. Gnot, Mechanisms of non-toxic anticorrosive pigments in organic waterborne 229 coatings, Prog. Org. Coat. 49 (2004) 359-371. otwiera się w nowej karcie
- G. Williams, H.N. McMurray, M. J. Loveridge, Inhibition of corrosion-driven organic coating 231 disbondment on galvanised steel by smart release group II and Zn(II)-exchanged bentonite pigments, 232 otwiera się w nowej karcie
- Electrochim. Acta. 55 (2010) 1740-1748. otwiera się w nowej karcie
- V. Ashworth, C.J.L. Booker. Cathodic protection: Theory and practice, John Wiley and Sons, New
- York, 1986. otwiera się w nowej karcie
- Seong-Jong Kim, Masazumi Okido, Kyung-Man Moon, An electrochemical study of cathodic 236 protection of steel used for marine structures, Korean J. Chem. Eng. 20 (2003) 560-565. otwiera się w nowej karcie
- F. Gan, Z. W. Sun, G. Sabde, D. T. Chin, Cathodic Protection to Mitigate External Corrosion of 238 otwiera się w nowej karcie
- Underground Steel Pipe Beneath Disbonded Coating, Corros. Eng. 50 (1994) 804-816. otwiera się w nowej karcie
- K. Zakowski, Studying the effectiveness of a modernized cathodic protection system for an offshore 240 platform, Anti-Corros. Method. M. 58 (2011) 167-172. otwiera się w nowej karcie
- L. Martinez, L. V. Žulj, F. Kapor, Disbonding of underwater-cured epoxy coating caused by cathodic 242 protection current, Corr. Sci. 51 (2009) 2253-2258. otwiera się w nowej karcie
- Y. R. Yoo, H. H. Cho, S. Take, J. G. Kim, Y. S. Kim, Influence of cathodic protection on the lifetime 244 extension of painted steel structures, Met. Mater. Int. 12 (2006) 255-261. otwiera się w nowej karcie
- E. L. Koehler, The Mechanism of Cathodic Disbondment of Protective Organic Coatings-Aqueous 246 Displacement at Elevated pH, Corr. Sci. 40 (1984) 5-8. otwiera się w nowej karcie
- T. Kamimura, H. Kishikawa, Mechanism of Cathodic Disbonding of Three-Layer Polyethylene- 248 otwiera się w nowej karcie
- Coated Steel Pipe, Corr. Sci. 54 (1998) 979-987. otwiera się w nowej karcie
- C.F. Barth, A. R. Troiano, Cathodic Protection and Hydrogen in Stress Corrosion Cracking, Corrosion 250 28 (1972) 259-263. otwiera się w nowej karcie
- L.H. Wolfe, C.C. Burnette, M.W. Joosten, Hydrogen embrittlement of cathodically protected subsea 252 bolting alloys, Mater. Performance 32 (1993).
- D, Festy, Cathodic Protection of Steel in Deep Sea: Hydrogen Embrittlement Risk and Cathodic 254 Protection Criteria, Corrosion 2001, Conference materials. otwiera się w nowej karcie
- 16. R. W. Bosch, J. Hubrecht, W. F. Bogaerts, B. C. Syrett, Electrochemical Frequency Modulation: A 256 New Electrochemical Technique for Online Corrosion Monitoring, Corr. Sci. 57(2001) 60-70. otwiera się w nowej karcie
- C. Andrade, C. Alonso, Corrosion rate monitoring in the laboratory and on-site, Constr. Build. Mater. 258 10 (1996) 315-328. otwiera się w nowej karcie
- J. P. Broomfielda, K. Davies, K. Hladky, The use of permanent corrosion monitoring in new and 260 existing reinforced concrete structures, Cement Concrete Comp. 24 (2002) 27-34. otwiera się w nowej karcie
- K. Zakowski, W. Sokolski, 24-hour characteristic of interaction on pipelines of stray currents leaking 262 from tram tractions, Corr. Sci. 41 (1999) 2099-2111. otwiera się w nowej karcie
- K. Żakowski, K. Darowicki, Methods of Evaluation of the Corrosion Hazard Caused by Stray Currents 264 to Metal Structures Containing Aggressive Media, Pol. J. Environ. Stud. 9 (2000) 237-241.
- K. Zakowski, K. Darowicki, Diagnosis of Reference Electrodes in Cathodic Protection Systems by 266 otwiera się w nowej karcie
- Electrochemical Impedance Spectroscopy, Corros. Rev. 20 (2011) 391-402. otwiera się w nowej karcie
- Guofu Qiao, Jinping Oua, Corrosion monitoring of reinforcing steel in cement mortar by EIS and 268 otwiera się w nowej karcie
- ENA, Electrochim Acta 52 (2007) 8008-819.
- M. Szocinski, K. Darowicki, Local impedance spectra of organic coatings, Polym. Degrad. Stabil. 98 270 (2013) 261-265. otwiera się w nowej karcie
- S. Krakowiak, K. Darowicki, Inspection of rubber linings operating in flue gas desulphurisation units, 272 otwiera się w nowej karcie
- Prog. Org. Coat. 46 (2003) 211-215. otwiera się w nowej karcie
- K. Darowicki, P. Slepski, M. Szocinski, Application of the dynamic EIS to investigation of transport 274 within organic coatings, Prog. Org. Coat. 52 (2005) 306-310. otwiera się w nowej karcie
- 26. NACE International, NACE No. 2/SSPC-SP 10 White Metal Blast Cleaning. otwiera się w nowej karcie
- 27. ASTM International. ASTM D1141 -98 Standard Practice for the Preparation of Substitute Ocean 277 otwiera się w nowej karcie
- Water, 2013. otwiera się w nowej karcie
- Źródła finansowania:
-
- grant NCBiR nr 2012/05/N/ST8/02899
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 103 razy