Characterization of magnesium doped lanthanum orthoniobate synthesized by molten salt route

Abstrakt

Molten salt synthesis method has been used to prepare the single phase magnesium doped lanthanum orthoniobate. The phase composition has been checked by X-ray diffraction method and the microstructure studies have been performed by scanning electron microscopy. The high temperature properties of the material have been investigated by thermogravimetry and electrochemical impedance spectroscopy. A dependence between sample total conductivity and temperature has been found supporting the thesis that there is strong correlation between apparent activation energy of conductivity and structural phase transition at ~500 °C. It has been also shown that the conductivity of magnesium doped lanthanum orthoniobate synthesized by the molten salt route reaches values of ~1 mS/cm at 720°C in wet hydrogen.

Cytowania

  • 1 8

    CrossRef

  • 0

    Web of Science

  • 1 8

    Scopus

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:
CERAMICS INTERNATIONAL nr 41, wydanie 6, strony 7847 - 7852,
ISSN: 0272-8842
Język:
angielski
Rok wydania:
2015
Opis bibliograficzny:
Mielewczyk-Gryń A., Wachowski S., Zagórski K., Jasiński P., Gazda M.: Characterization of magnesium doped lanthanum orthoniobate synthesized by molten salt route// CERAMICS INTERNATIONAL. -Vol. 41, iss. 6 (2015), s.7847-7852
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ceramint.2015.02.121
Weryfikacja:
Politechnika Gdańska

wyświetlono 171 razy

Publikacje, które mogą cię zainteresować

Meta Tagi