Comprehensive Investigation of Stoichiometry–Structure–Performance Relationships in Flexible Polyurethane Foams
Abstrakt
Polyurethane (PU) foams are versatile materials with a broad application range. Their performance is driven by the stoichiometry of polymerization reaction, which has been investigated in several works. However, the analysis was often limited only to selected properties and compared samples differing in apparent density, significantly influencing their performance. In the bigger picture, there is still a lack of comprehensive studies dealing with the stoichiometry impact on PU foams’ performance. Herein, flexible PU foams with a similar apparent density but differing in the isocyanate index (IIso) (from 0.80 to 1.20) were prepared. The stoichiometry–structure–performance relationships were investigated considering cellular and chemical structure, as well as the static and dynamic mechanical properties, thermal stability, thermal insulation, and acoustic performance. For IIso of 1.00, the biggest cell diameters of 274 µm were noted, which was 21–25% higher compared to 0.80 and 1.20 values. Increasing IIso reduced open cell content from 83.1 to 22.4%, which, combined with stiffening of structure (rise of modulus from 63 to 2787 kPa) resulting from crosslinking, limited the sound suppression ability around five times. On the other hand, it significantly strengthened the material, increasing tensile and compressive strength 4 and 13 times, respectively. Changes in the foams’ performance were also induced by the glass transition temperature shift from 6.1 to 31.7 ◦C, resulting from a greater extent of urethane groups’ generation and additional isocyanate reactions. Generally, the presented work provides important insights into preparing flexible PU foams and could be very useful for the future development of these materials.
Cytowania
-
1 5
CrossRef
-
0
Web of Science
-
1 5
Scopus
Autorzy (9)
-
Adam Piasecki
- Politechnika Poznańska
-
Mateusz Barczewski
- Politechnika Poznańska
-
Roman Barczewski
- Politechnika Poznańska
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/polym14183813
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Polymers
nr 14,
ISSN: 2073-4360 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Olszewski A., Kosmela P., Piasecki A., Żukowska W., Szczepański M., Wojtasz P., Barczewski M., Barczewski R., Hejna A.: Comprehensive Investigation of Stoichiometry–Structure–Performance Relationships in Flexible Polyurethane Foams// Polymers -Vol. 14,iss. 18 (2022), s.3813-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/polym14183813
- Źródła finansowania:
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 152 razy