Single crystals of a new ternary aluminide ErV2Al20 were grown using a self-flux method. The crystal structure was determined by powder X-ray diffraction measurements and Rietveld refinement, and physical properties were studied by means of electrical resistivity, magnetic susceptibility and specific heat measurements. These measurements reveal that ErV2Al20 is a Curie-Weiss paramagnet down to 1.95 K with an effective magnetic moment μeff =9.27(1) μB and Curie-Weiss temperature ΘCW =−0.55(4) K. The heat capacity measurements show a broad anomaly at low temperatures that is attributed to the presence of a low-energy Einstein mode with characteristic temperature ΘE =44 K, approximately twice as high as in the isostructural ‘Einstein solid’ VAl10.1.
Cytowania
-
2 3
CrossRef
-
0
Web of Science
-
2 3
Scopus
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jssc.2016.09.029
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF SOLID STATE CHEMISTRY
nr 245,
strony 10 - 16,
ISSN: 0022-4596 - Język:
- angielski
- Rok wydania:
- 2017
- Opis bibliograficzny:
- Winiarski M., Klimczuk T.: Crystal structure and low-energy Einstein mode in ErV2Al20 intermetallic cage compound// JOURNAL OF SOLID STATE CHEMISTRY. -Vol. 245, (2017), s.10-16
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jssc.2016.09.029
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 160 razy
Publikacje, które mogą cię zainteresować
Structural and physical characterization of NpPt2In7
- T. Klimczuk,
- A. Shick,
- S. Khmelevskyi
- + 6 autorów
Structure redetermination, transport and thermal properties of the YNi3Al9 compound
- I. Oshchapovskyy,
- E. E. Oyeka,
- T. Tran
- + 2 autorów