Evaluation of structural and electrical properties of multicomponent spinel oxide thin films deposited via spray pyrolysis technique
Abstrakt
This work reports the preparation of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited layers were amorphous, and crystallised upon heat treatment at 500 ◦C. Microstructural analyses proved a homogeneous elemental distribution and the desired Fd-3 m cubic spinel structure. Electrical conductivity measurements indicated a dependence on the processing temperature, with the highest electrical conductivity values (~3 S cm 1 at 700 ◦C) obtained for layers heat-treated at 700 ◦C. The spray pyrolysis technique seems to be well suited to fabricating and exploring spinel-based high-entropy oxides synthesized as thin films, and to studying new compositions containing transition metal cations.
Cytowania
-
7
CrossRef
-
0
Web of Science
-
5
Scopus
Autorzy (5)
-
Grzegorz Cempura dr inż.
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.matchar.2023.113097
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
MATERIALS CHARACTERIZATION
nr 203,
ISSN: 1044-5803 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Kamecki B., Karczewski J., Cempura G., Jasiński P., Molin S.: Evaluation of structural and electrical properties of multicomponent spinel oxide thin films deposited via spray pyrolysis technique// MATERIALS CHARACTERIZATION -Vol. 203, (2023), s.113097-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.matchar.2023.113097
- Źródła finansowania:
- Weryfikacja:
- Politechnika Gdańska
Powiązane datasety
- dane badawcze SEM/EDX data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
- dane badawcze TEM data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
- dane badawcze XRD data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe, annealed in a range from 400 to 900oC
- dane badawcze Total electrical conductivity data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
wyświetlono 112 razy
Publikacje, które mogą cię zainteresować
Microstructure and Electrical Properties of Fe,Cu Substituted (Co,Mn)3O4 Thin Films
- D. Grudzień,
- S. Molin,
- P. V. Hendriksen
- + 1 autorów
Properties of Barium Cerate-Zirconate Thin Films
- P. Winiarz,
- M. S. Covarrubias Campos,
- M. Sriubas
- + 6 autorów