Fracture surface topography investigation and fatigue life assessment of notched austenitic steel specimens
Abstrakt
The objectives of this study were to investigate the fracture surface topography of X8CrNiS18-9 austenitic stainless-steel specimens for different loadings and notch radii and to supplement the knowledge about the fracture mechanisms for fatigue performance. Cases with three different values of the notch radius ρ and the stress amplitude σa were analysed. The fracture topographies were quantified by the areas over their entire surfaces with the aid of an optical confocal measurement system. The results showed a well-correlated root mean square height Sq and void volume Vv, identifying the characteristics of the entire fracture method. A fracture surface topography fatigue damage model was developed based on the product of the stress amplitude σa by the Sq to the Vv ratio. Overall, the predictions were close to the fatigue lives found in the experiments.
Cytowania
-
2 8
CrossRef
-
0
Web of Science
-
2 7
Scopus
Autorzy (4)
-
Grzegorz Robak
-
Krzysztof Żak
-
Ricardo Branco
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.engfailanal.2022.106121
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
ENGINEERING FAILURE ANALYSIS
nr 135,
ISSN: 1350-6307 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Macek W., Robak G., Żak K., Branco R.: Fracture surface topography investigation and fatigue life assessment of notched austenitic steel specimens// ENGINEERING FAILURE ANALYSIS -Vol. 135, (2022), s.106121-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.engfailanal.2022.106121
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 124 razy
Publikacje, które mogą cię zainteresować
Fractographic-fractal dimension correlation with crack initiation and fatigue life for notched aluminium alloys under bending load
- W. Macek,
- D. Rozumek,
- S. Faszynka
- + 3 autorów
Effect of bending-torsion on fracture and fatigue life for 18Ni300 steel specimens produced by SLM
- W. Macek,
- R. Masoudi Nejad,
- S. Zhu
- + 5 autorów
Fatigue fracture surface metrology of thin-walled tubular austenitic steel specimens after asynchronous loadings
- W. Macek,
- Ł. Pejkowski,
- R. Branco
- + 2 autorów