Influence of dopants on structure of polycrystalline bismuth niobate

Abstrakt

Bismuth niobate (BiNbO4) has attracted attention as a low-fired ceramics with promising microwave application potential. BiNbO4 ceramics was fabricated by mixed oxide method and sintered at temperature T<1000˚C. As the sintering aids a small amount of CuO oxide was used. The crystalline structure of the ceramic samples was examined by X-ray diffraction method at room temperature. The Rietveld refinement method was used for analysis of diffraction data. As a result an influence of dopants on crystal structure of bismuth niobate (BiNbO4) ceramics was revealed. It was found that fabricated BiNbO4 ceramics adopted the orthorhombic symmetry (αBiNbO4 phase, Pnna (52) space group). Small differences in elementary cell parameters were found.

Cytowania

  • 0

    CrossRef

  • 1

    Web of Science

  • 0

    Scopus

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
Opublikowano w:
Advances in Materials Science nr 18, strony 35 - 41,
ISSN: 1730-2439
Język:
angielski
Rok wydania:
2018
Opis bibliograficzny:
Czekaj D., Lisińska-Czekaj A.: Influence of dopants on structure of polycrystalline bismuth niobate// Advances in Materials Science. -Vol. 18., iss. 4 (2018), s.35-41
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1515/adms-2017-0048
Weryfikacja:
Politechnika Gdańska

wyświetlono 13 razy

Publikacje, które mogą cię zainteresować

Meta Tagi