Influence of the Tool Rotational Speed on Physical and Chemical Properties of Dissimilar Friction-Stir-Welded AA5083/AA6060 Joints
Abstrakt
Aluminum alloys have been successfully used in the railroad and automotive industries because of their potential to significantly reduce component weights, and their good mechanical and anti-corrosion properties. Problems with joining aluminum alloys are characterized by low weldability, which influences the need for studies focused on unconventional methods. The environmentally friendly and low-cost friction-stir-welding method enables the material to be joined without melting. In the following study, dissimilar butt joints were produced from AA5083 and AA6060 alloys. A constant tool traverse speed of 100 mm/min and a tool tilt angle of 2º were used, combined with tool rotational speeds of 800, 1000 and 1200 RPM. It was revealed that as the tool speed increases, the hardness in the weld nugget zone increases, due to higher heat input and more effective recrystallization. The highest hardness of the mweld nugget zone was observed for the weld that was produced with the highest tool rotational speed, and was equal to 1.07 GPa, compared to the hardness of both parent materials of 0.75 and 1.15 GPa for AA5083 and AA6060, respectively. mIncreasing the heat input also decreased the hardness of the heat-affected zone, where recrystallization was not bobserved. The lowest density of dislocations with the highest mobility was observed in the heat-affected zone on the AA6060 side, which also contributed to the reduction in strength in this zone. The produced welds exhibited corrosion resistance between both parent materials, with the lowest corrosion current density being 6.935 ± 0.199 µA·cm–2 for the weld that was produced at a tool speed of 1200 RPM.
Cytowania
-
1 0
CrossRef
-
0
Web of Science
-
1 0
Scopus
Autorzy (4)
-
Pasquale Cavaliere
- Department of Innovation Engineering, University of Salento, Via per Arnesano, 73100 Lecce, Italy
-
Angelo Perrone
- Department of Innovation Engineering, University of Salento, Via per Arnesano, 73100 Lecce, Italy
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/met12101658
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Metals
nr 12,
ISSN: 2075-4701 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Laska A., Szkodo M., Cavaliere P., Perrone A.: Influence of the Tool Rotational Speed on Physical and Chemical Properties of Dissimilar Friction-Stir-Welded AA5083/AA6060 Joints// Metals -Vol. 12,iss. 12, 1658 (2022), s.1-21
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/met12101658
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 111 razy