Fatigue behaviour of SLM 18Ni300 steel under proportional bending-torsion loading is studied. The fatigue tests are conducted under pulsating loading conditions using tubular specimens with a transversal circular hole. Three ratios of the normal stress to shear stress are considered, namely σ/τ=4,σ/τ=2 and σ/τ = 4/3. Crack initiation sites were found for two diametrically opposite points around the hole, whose locations are governed by the loading scenario. Crack angles at the early stage of growth were successfully predicted from the first principal direction at the nodes with maximum values of the first principal stress at the hole. Fatigue crack initiation life was estimated based on the SWT parameter, defined from uniaxial low-cycle fatigue tests performed for smooth standard specimens under fully reversed strain-controlled conditions. Overall, predicted lives are in agreement with the experiments.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (6)
-
Ricardo Branco
-
José Domingos Costa
-
J. A. M. Ferreira
-
C. Capela
-
Filippo Berto
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja monograficzna
- Typ:
- rozdział, artykuł w książce - dziele zbiorowym /podręczniku w języku o zasięgu międzynarodowym
- Opublikowano w:
-
Structural Integrity
nr 25,
strony 161 - 168,
ISSN: 2522-560X - Tytuł wydania:
- Structural Integrity and Fatigue Failure Analysis strony 161 - 168
- Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Branco R., Costa J. D., Ferreira J. A. M., Capela C., Berto F., Macek W.: Multiaxial Fatigue Behaviour of SLM 18Ni300 Steel// Structural Integrity and Fatigue Failure Analysis/ : , 2022, s.161-168
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/978-3-030-91847-7_16
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 113 razy
Publikacje, które mogą cię zainteresować
Effect of bending-torsion on fracture and fatigue life for 18Ni300 steel specimens produced by SLM
- W. Macek,
- R. Masoudi Nejad,
- S. Zhu
- + 5 autorów
Notch fatigue analysis and life assessment using an energy field intensity approach in 7050-T6 aluminium alloy under bending-torsion loading
- R. Branco,
- J. D. Costa,
- L. Borrego
- + 2 autorów
On the use of uniaxial one-parameter damage laws for estimating fatigue life under multiaxial loading
- R. Branco,
- J. D. Costa,
- L. Borrego
- + 3 autorów
Load path sensitivity and multiaxial fatigue life prediction of metals under non-proportional loadings
- Q. Deng,
- S. Zhu,
- X. Niu
- + 3 autorów