Orientation effects on the fracture behaviour of additively manufactured stainless steel 316L subjected to high cyclic fatigue
Abstrakt
In this paper, stainless steel 316L (SS316L) bars were additively manufactured (AM) in three orientations (Z – vertical, XY – horizontal, ZX45 – midway between vertical and horizontal) by using the Laser Powder Bed Fusion Melting (LPBF-M) method. The AM specimens were subjected to load control fatigue testing under full tension and compression (R = -1) at stress amplitudes ±350, ±400 and ±450 MPa. The XY and ZX45 printing orientations were found to significantly improve service life. Although similar strain response was found for each orientation when the same stress amplitude was applied, slightly different fracture mechanisms were identified during the post-mortem surface observations.
Cytowania
-
1
CrossRef
-
0
Web of Science
-
2
Scopus
Autorzy (5)
-
Gunputh Urvashi
-
Zbigniew Kowalewski profesor
-
Paul Wood
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
THEORETICAL AND APPLIED FRACTURE MECHANICS
ISSN: 0167-8442 - Język:
- angielski
- Rok wydania:
- 2024
- Opis bibliograficzny:
- Kopec M., Urvashi G., Macek W., Kowalewski Z., Wood P.: Orientation effects on the fracture behaviour of additively manufactured stainless steel 316L subjected to high cyclic fatigue// THEORETICAL AND APPLIED FRACTURE MECHANICS -, (2024),
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.tafmec.2024.104287
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 58 razy
Publikacje, które mogą cię zainteresować
Strain energy density and entire fracture surface parameters relationship for LCF life prediction of additively manufactured 18Ni300 steel
- W. Macek,
- R. Branco,
- J. de Jesus
- + 4 autorów
Quasistatic and fatigue behavior of an AISI H13 steel obtained by additive manufacturing and conventional method
- J. F. Garcias,
- R. F. Martins,
- R. Branco
- + 4 autorów