A study on a novel material - manganese borosilicate glass without alkali metals, was reported. It was found that the obtained samples containing high amount of manganese oxide (60MnO–xSiO2–(40 − x)B2O3, x = 5, 10, 15, 20 and 30 mol%) were amorphous and homogeneous. XPS measurements showed that most of manganese ions are at oxidation level of Mn2 + ions and the mean oxidation level slightly moves toward higher value, with increasing in SiO2 content. The conductivity was described in the terms of thermally activated polaron hopping with a charge carrier centred on Mn ions. It was shown, that the conductivity strongly depends on the mean Mn–Mn distance. Keywords: Electrical property; Oxides; Glass; Polaron hopping
Cytowania
-
1 0
CrossRef
-
0
Web of Science
-
1 0
Scopus
Autorzy (6)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF NON-CRYSTALLINE SOLIDS
nr 458,
strony 15 - 21,
ISSN: 0022-3093 - Język:
- angielski
- Rok wydania:
- 2017
- Opis bibliograficzny:
- Kupracz P., Lenarciak A., Łapiński M., Prześniak-Welenc M., Wójcik N., Barczyński R.: Polaron hopping conduction in manganese borosilicate glass// JOURNAL OF NON-CRYSTALLINE SOLIDS. -Vol. 458, (2017), s.15-21
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jnoncrysol.2016.12.008
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 185 razy
Publikacje, które mogą cię zainteresować
Mechanism of hopping conduction in Be–Fe–Al–Te–O semiconducting glasses and glass–ceramics
- N. Wójcik,
- N. S. Tagiara,
- D. Möncke
- + 4 autorów