The effect of preliminary creep-strain on material behavior under LCF tension/compression and pure torsion regimes

Abstrakt

This paper presents the results of experimental tests of monotonic tension and torsion, creep-rupture and preliminary creep at 200C and 300C, as well as low-cycle fatigue of 2024 T3511 aluminum alloy. The fatigue process was conducted at room temperature for uniaxial tension/compression and torsion. The as-received material and pre-deformed material were also investigated during creep at elevated temperature. Basic monotonic, creep and fatigue characteristics of the material were determined. Detailed micro- and macroscopic analyses of fracture surfaces (scanning electron microscopy, SEM) were carried out. The influence of different creep pre-deformation histories at elevated temperature on the behavior of the studied alloy were characterized with respect to monotonic and cyclic loads at room temperature.

Cytowania

  • 2

    CrossRef

  • 0

    Web of Science

  • 2

    Scopus

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach
Opublikowano w:
INTERNATIONAL JOURNAL OF FATIGUE nr 178,
ISSN: 0142-1123
Język:
angielski
Rok wydania:
2024
Opis bibliograficzny:
Tomczyk A., Grodzki W., Seweryn A.: The effect of preliminary creep-strain on material behavior under LCF tension/compression and pure torsion regimes// INTERNATIONAL JOURNAL OF FATIGUE -Vol. 178, (2024), s.108017-
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ijfatigue.2023.108017
Źródła finansowania:
  • Research project no.2018/29/B/ST8/00697 (National Science Centre of Poland) and realized in Bialystok University of Technology
Weryfikacja:
Politechnika Gdańska

wyświetlono 102 razy

Publikacje, które mogą cię zainteresować

Meta Tagi