The preparation and evaluation of core-shell magnetic dummy-template molecularly imprinted polymers for preliminary recognition of the low-mass polybrominated diphenyl ethers from aqueous solutions

Mariusz Marć; Piotr Paweł Wieczorek

doi:10.1016/j.scitotenv.2020.138151

The preparation and evaluation of core-shell magnetic dummy-template molecularly imprinted polymers for preliminary recognition of the low-mass polybrominated diphenyl ethers from aqueous solutions

Abstrakt

The design, preparation process, binding abilities, morphological characteristic and prospective field of application of dummy-template magnetic molecularly imprinted polymer (DMMIP) for preliminary recognition of the selected low-mass polybrominated diphenyl ethers (PBDE-47 and PBDE-99) from aquatic environment were investigated. The surface of iron oxide (Fe3O4) nanopowder (50-100 nm particles size) was modified with tetraethoxysilane and next prepared Fe3O4@SiO2 particles were dispersed in anhydrous toluene functionalized by (3-aminopropyl)triethoxysilane. Finally, MIPs' thin film layer on the surface of Fe3O4@SiO2@NH2 was formed in acetonitrile as a solvent solution, using ethylene glycol dimethacrylate as the cross-linker, building monomer, 1,1′-Azobis(cyclohexanecarbonitrile) as the radical initiator, methacrylic acid as a functional monomer and 4,4'- Dihydroxydiphenyl ether as the dummy template molecule as a structural analogue of low-mass PBDEs. To characterize the chemical structure of prepared DMMIPs, the Fourier transform infrared spectroscopy analysis was performed. The specific surface area of the developed sorbent was estimated using Brauner-Emmet-Teller nitrogen adsorption/desorption analysis. To assess the average pore sizes, pore diameters and pore volumes of the prepared sorbent, the Barret-Joyner-Halenda technique was applied. The average values of imprinting factor for PBDE-47 and PBDE-99 were 11.3 ± 1.6 and 13.7 ± 1.2, respectively. The average value of recovery of PBDE-47 and PBDE-99 for developed DMMIPs from modelling water : methanol solution were 85.4 ± 6.7% and 86.4 ± 9.4%, respectively. In a case of spiked distilled water, tap water as well as local river water the calculated recovery values ranged from 65%% up to 82% and from 33% up to 76% for PBDE-47 and PBDE-99, respectively. Following the preliminary research on selected water samples, the proposed combination of imprinting technology and core–shell materials with magnetic properties might be considered as a promising sorption tool used for targeted recognition of low-mass PBDEs in aquatic solutions.

Cytowania

2 4

CrossRef
0

Web of Science
2 2

Scopus

Autorzy (2)

Mariusz Marć dr hab. inż.
Piotr Paweł Wieczorek prof. dr hab. inż.

Cytuj jako

Pełna treść

pobierz publikację

pobrano 70 razy

Wersja publikacji: Accepted albo Published Version
Licencja: otwiera się w nowej karcie

Słowa kluczowe

Informacje szczegółowe

Kategoria:

Publikacja w czasopiśmie

Typ:

artykuły w czasopismach

Opublikowano w:

SCIENCE OF THE TOTAL ENVIRONMENT nr 724,
ISSN: 0048-9697

Język:

angielski

Rok wydania:

2020

Opis bibliograficzny:

Marć M., Wieczorek P.: The preparation and evaluation of core-shell magnetic dummy-template molecularly imprinted polymers for preliminary recognition of the low-mass polybrominated diphenyl ethers from aqueous solutions// SCIENCE OF THE TOTAL ENVIRONMENT -Vol. 724, (2020), s.138151-

DOI: