The σ-phase superconductors Nb20.4Rh5.7Ge3.9 and Nb20.4Rh5.7Si3.9

Abstrakt

We show that the previously unreported ternary σ phases Nb20.4Rh5.7Ge3.9 and Nb20.4Rh5.7Si3.9 are both superconductors with Tc values of approximately 1.9 K. The superconducting transitions were characterized through temperature-dependent magnetic susceptibility, electrical resistance, and specific heat measurements. The Sommerfeld constants, γ, for Nb20.4Rh5.7Ge3.9 and Nb20.4Rh5.7Si3.9 are 89(1) mJ mol-f.u.−1K−2 and 86(1) mJ mol-f.u.−1K−2 (about 3.0 and 2.9 mJ mol-atom−1 K−2), respectively. The normalized specific heat jumps at Tc, ΔC/γTc, are approximately 1.39 for Nb20.4Rh5.7Ge3.9 and 1.30 for Nb20.4Rh5.7Si3.9, consistent with both materials being weakly coupled BCS type superconductors.

Cytowania

2

CrossRef
0

Web of Science
2

Scopus

Autorzy (4)

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

pełna treść artykułu zobacz w serwisie zewnętrznym otwiera się w nowej karcie

Słowa kluczowe

NADPRZEWODNICTWO

Informacje szczegółowe

Kategoria:: Publikacja w czasopiśmie
Typ:: artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:: SOLID STATE COMMUNICATIONS nr 284-286, strony 96 - 101,
ISSN: 0038-1098
Język:: angielski
Rok wydania:: 2018
Opis bibliograficzny:: Carnicom E., Kong T., Klimczuk T., Cava R.: The σ-phase superconductors Nb20.4Rh5.7Ge3.9 and Nb20.4Rh5.7Si3.9// SOLID STATE COMMUNICATIONS. -Vol. 284-286, (2018), s.96-101
DOI:: Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ssc.2018.09.014
Weryfikacja:: Politechnika Gdańska