The presence of the oxide layers on Zr alloys may retard or enhance the hydrogen entry and material degradation, depending on the layer features. This research has been aimed to determine the effects of pre-oxidation of the Zircaloy-2 alloy at a different temperature on hydrogen degradation. The specimens were oxidised in laboratory air at 350°C, 700°C, and 900°C. After, some samples were tensed at 10-5 strain rate and simultaneously...
The purpose of the present research was to determine the oxidation and hydrogenation behavior in the new Zr-2Mn alloy. The oxidation of alloy was performed at temperatures between 350°C and 900°C for 30 minutes. The hydrogen charging was made for 72 h at a current density 80 mA/cm2. The charged samples were heat treated at 400°C for 4 h to obtain a uniform hydrogen profile content across the sample. The oxidation resulted in an...
The objective of the present project was to determine the effects of powder granulation (fraction of grain size) for the Ti-13Nb-13Zr alloy, produced by powder metallurgy, on its porosity, grain cohesion, compressive strength, and Young`s modulus. Two powder fractions, 45–105 µm, and 106–250 µm were applied. The 50 mass pct of NH4HCO3 was added as a space holder. The specimens were in compaction stage uniaxially pressed at pressure...
wyświetlono 59 razy