High temperature corrosion evaluation and lifetime prediction of porous Fe22Cr stainless steel in air in temperature range 700–900 °C
This work describes a high temperature corrosion kinetics study of ~30% porous Fe22Cr alloys. The surface area of the alloy (~0.02 m2 g-1) has been determined by tomographic microscopy. The weight gain of the alloys was studied by isothermal thermogravimetry in the air for 100 hours at 700 - 900 °C. Breakaway oxidation was observed after oxidation at 850 °C (~100 hours) and 900 °C (~30 hours). The lifetime prediction shows the...
-
Hydrogen direct reduction and reoxidation behaviour of high-grade pellets
High grade pellets with basicity index close to 0.5 were directly reduced in pure hydrogen atmosphere. The reduction experiments were performed in the temperature range 800 e1000 C at the pressure of 8 bar. The pellets internal structure was analysed through micro tomography observations in the unreduced and reduced conditions. After reduction, the pellets showed a variation of porosity up to more than 15% with a remarkable change...
-
Direct reduction of pellets through hydrogen: Experimental and model behaviour
This paper presents the hydrogen reduction behaviour of industrial pellets designed for the efficient hydrogen based direct reduction. The pellets were provided with very low non ferrous oxides percentage (0.52 of basicity index) and with the absence on TiO2 oxides. The pellets measured diameters in the range 1.14–1.72 cm and were characterized in terms of porosity, pores size, tortuosity and compression strength. The pellets were...