This article reports the effect of underwater wet welding parameters and conditions on the diffusible hydrogen content in deposited metal for welding with a self-shielded flux cored wire. The diffusible hydrogen content in deposited metal was determined using the glycerin method according to the Plackett-Burman design determining the significance of the effect of the stick out length, welding current, arc voltage, travel speed...
The article presents the idea of the use of Temper Bead Welding (TBW) technique to improve the weldability of high strength steel at underwater wet welding conditions. Wet welding method with the use of covered electrodes is described. This work shows results of metallographic examinations and hardness measurements of samples of S420G2+M steel with weld beads performed under water. It has been shown that Temper Bead Welding technique...
The normalized S355G10 + N steel was chosen for testing, it is used in a variety of applications including the building of offshore structures, which may require repairs in water environment. The main aim of the work was to check susceptibility to cold cracking for fillet welds – Controlled Thermal Severity (CTS) tests and butt welds – Tekken tests and in the next step evaluation of effectiveness of Temper Bead Welding (TBW) application...
Uzyskane stopnie/tytuły naukowe
Nadanie stopnia naukowegodr inż. Budowa i eksploatacja maszyn (Dziedzina nauk technicznych)
wyświetlono 395 razy