Spinel oxides with the general formula Mn1.7Cu1.3-xFexO4 (x= 0, 0.1, 0.3, 0.5) were prepared and evaluated in this work for their properties at high temperatures. The effect of partially substituting Cu by Fe has not been studied so far for this group of materials and is thus evaluated in this work. Mn1.7Cu1.3-xFexO4 powders were synthesised by a soft chemistry process and studied in terms of crystallographic phase analysis, electrical...

A dual surface modification of an SOFC metallic interconnect with a Gd2O3 layer and an MnCo2O4 coating was evaluated. The tested samples were oxidized for 7000 h in air at 1073 K. Oxidation products were characterized using XRD, SEM-EDS, and confocal Raman imaging, and ASR was measured. The effect of gadolinium segregation at grain boundaries in Cr2O3 was evaluated using S/TEM-EDS. Area specific-resistance was measured and fuel...

Development of environmentally friendly, high performing oxygen evolution reaction (OER) catalysts is an important research challenge. In this work, iron doped strontium titanates with a general formula SrTi1-xFexO3-δ (x = 0.35, 0.50, 0.70, 0.90, and 1.00) denoted as STFx, were synthesized via a solid state reaction technique and characterized in terms of oxygen evolution reaction electrocatalysis in an alkaline electrolyte (0.1...