The article presents the results of mechanical and tribological tests of Ni-P/Si3N4 nanocomposite coatings deposited on the AW-7075 aluminum alloy using the chemical reduction method. The influence of the chemical composition on the Vickers microhardness determined by the DSI method was examined. The nanocomposite layers were made of Si3N4 silicon nitride in a polydisperse powder with a particle size ranging from 20 to 25 nm. The...

The article presents the results of tribological tests of Ni-P/Si3N4 nanocomposite and Ni-P nickel layers deposited on the AW-7075 aluminum alloy by chemical reduction method, and the AW-7075 alloy without coating. Nanocomposite layers were produced using Si3N4 siliconnitride in the form of a polydisperse powder whose particle sizes ranged from 20 to 25 nm. The influence of the content of the dispersion phase layer material on...

Przedstawiono wpływ obecności grafitu jako fazy dyspersyjnej na właściwości mechaniczne warstw hybrydowych Ni-P/Si3N4/grafit, które osadzono metodą redukcji chemicznej na stopie glinu AW-7075. Wykonano badania morfologii powierzchni warstw metodą mikroskopii świetlnej i skaningowej. Dalszą część pracy stanowiły badania mechaniczne, czyli pomiary mikrotwardości warstw oraz ich adhezji do aluminiowego podłoża, a także analizy wpływu...