The study presents a research capabilities of Dynamic Electrochemical Impedance Spectroscopy (DEIS) as a tool used for instantaneous on-line monitoring of corrosion processes on the example of AA 7075 aluminum alloy. A borate buffer with admixed chloride ions in a quantity ranging from 0.05 to 25 mM was used to represent different types of corrosion attack. The surface of samples specimens was evaluated before and after the tests...

The microstructure of aluminum alloys plays a key role in their corrosion resistance. In particular, the presence of intermetallic precipitates differing in the potential from the alloy matrix induces local corrosion. The study presents the effect of native air-formed oxidation on the corrosion behavior of AA 7075 aluminum alloy. Various microscopic and spectroscopic techniques were used to examine the changes occurring in the...

Celem pracy były pomiary korozyjności kondensatów pochodzących z kolumny destylacyjnej z dodatkiem neutralizatora oraz inhibitora korozji, ponadto przeprowadzono badania SEM i EDX produktów korozji pochodzących z rurek chłodnicy powietrznej. Wykazano, że znacznie większą agresywnością charakteryzują się kondensaty które pochodzą z przerobu ropy naftowej zawierającą slopy.